DSM Engineering Plastics Stanyl? TE263F6 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized, Impact Modified (North America)
Subcategory: Filled/Reinforced Thermoplastic; Nylon; Nylon 46; Polymer; Thermoplastic
Key Words: Polyamide 46
Material Notes:
Information provided by DSM Engineering Plastics.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.31 g/cc | 0.0473 lb/in? | ISO 1183 | |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH / 23?C; Similar to ISO 62 | |
Mechanical Properties |
||||
|
||||
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-1/-2 | |
| Elongation at Break | 5 % | 5 % | ISO 527-1/-2 | |
| Flexural Modulus | 6.3 GPa | 914 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 20 kJ/m? | 9.52 ft-lb/in? | ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 15 kJ/m? | 7.14 ft-lb/in? | at -40?C; ISO 180/1A | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 20 ?m/m-?C | 11.1 ?in/in-?F | parallel to flow; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 80 ?m/m-?C | 44.4 ?in/in-?F | ISO 11359-1/-2 | |
| Melting Point | 295 ?C | 563 ?F | ISO 11357-1/-3 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 ?C | 554 ?F | ISO 75-1/-2 | |
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.