DuPont Zytel? 153HSL NC010 Nylon 612
Subcategory: Nylon; Nylon 612; Polymer; Thermoplastic
Material Notes:
Zytel? 153HSL NC010 is a heat stabilized, lubricated polyamide 612 resin that is suitable for molding and extrusion.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.06 g/cc | 0.0383 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.06 g/cc | 0.0383 lb/in? | DAM; ASTM D 792 | |
| Water Absorption | 0.25 % | 0.25 % | Immersion 24h; 23?C; DAM; ASTM D 570 | |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 50%RH; 23?C; DAM; ISO 62, Similar to | |
| Water Absorption at Saturation | 3 % | 3 % | Immersed; 23?C; DAM; ISO 62, Similar to | |
| Water Absorption at Saturation | 3 % | 3 % | DAM; ASTM D 570 | |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Flow 3.2mm (0.125in) | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 2.0mm; ISO 294-4 | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell R | 114 | 114 | DAM; ASTM D 785 | |
| Tensile Strength, Ultimate | 41 MPa | 5950 psi | 77?C; DAM; ASTM D 638 | |
| Tensile Strength, Ultimate | 61 MPa | 8850 psi | DAM; ASTM D 638 | |
| Tensile Strength, Ultimate | 61 MPa | 8850 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Ultimate | 94 MPa | 13600 psi | -40?C; DAM; ASTM D 638 | |
| Tensile Strength, Ultimate | 94 MPa | 13600 psi | -40?C; 50%RH; ASTM D 638 | |
| Tensile Strength, Yield | 30 MPa | 4350 psi | 77?C; DAM; ASTM D 638 | |
| Tensile Strength, Yield | 51 MPa | 7400 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Yield | 53 MPa | 7690 psi | 50%RH; ISO 527 | |
| Tensile Strength, Yield | 61 MPa | 8850 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 62 MPa | 8990 psi | DAM; ISO 527 | |
| Tensile Strength, Yield | 93 MPa | 13500 psi | -40?C; 50%RH; ASTM D 638 | |
| Tensile Strength, Yield | 94 MPa | 13600 psi | -40?C; DAM; ASTM D 638 | |
| Elongation at Break | Min 300 % | Min 300 % | 50%RH; ASTM D 638 | |
| Elongation at Break | Min 50 % | Min 50 % | 50%RH; Nominal; ISO 527 | |
| Elongation at Break | 15 % | 15 % | -40?C; DAM; ASTM D 638 | |
| Elongation at Break | 150 % | 150 % | DAM; ASTM D 638 | |
| Elongation at Break | 30 % | 30 % | -40?C; 50%RH; ASTM D 638 | |
| Elongation at Break | 30 % | 30 % | DAM; Nominal; ISO 527 | |
| Elongation at Yield | 14 % | 14 % | ASTM D 638 | |
| Elongation at Yield | 19 % | 19 % | ISO 527 | |
| Elongation at Yield | 30 % | 30 % | ASTM D 638 | |
| Elongation at Yield | 4.4 % | 4.4 % | ISO 527 | |
| Elongation at Yield | 40 % | 40 % | ASTM D 638 | |
| Elongation at Yield | 7 % | 7 % | ASTM D 638 | |
| Elongation at Yield | 8 % | 8 % | ASTM D 638 | |
| Tensile Modulus | 1.6 GPa | 232 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 2.4 GPa | 348 ksi | DAM; ISO 527 | |
| Flexural Modulus | 0.41 GPa | 59.5 ksi | 77?C; DAM; ASTM D 790 | |
| Flexural Modulus | 1.24 GPa | 180 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 1.45 GPa | 210 ksi | 50%RH; ISO 178 | |
| Flexural Modulus | 2.03 GPa | 294 ksi | DAM; ASTM D 790 | |
| Flexural Modulus | 2.1 GPa | 305 ksi | DAM; ISO 178 | |
| Flexural Modulus | 2.3 GPa | 334 ksi | -40?C; DAM; ASTM D 790 | |
| Flexural Modulus | 2.8 GPa | 406 ksi | -40?C; 50%RH; ASTM D 790 | |
| Shear Strength | 59 MPa | 8560 psi | DAM; ASTM D 732 | |
| Izod Impact, Notched (ISO) | 4 kJ/m? | 1.9 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Notched (ISO) | 6 kJ/m? | 2.86 ft-lb/in? | 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 5 kJ/m? | 2.38 ft-lb/in? | -30?C; 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 5 kJ/m? | 2.38 ft-lb/in? | -30?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 0.4 J/cm? | 1.9 ft-lb/in? | -30?C; 50%RH; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 0.5 J/cm? | 2.38 ft-lb/in? | -30?C; DAM; ISO 179/1eA | |
| Charpy Impact, Unnotched Low Temp | NB | NB | -30?C; 50%RH; ISO 179/1eU | |
| Charpy Impact, Unnotched Low Temp | NB | NB | -30?C; DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.4 J/cm? | 1.9 ft-lb/in? | DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 0.7 J/cm? | 3.33 ft-lb/in? | 50%RH; ISO 179/1eA | |
| Izod Impact, Notched | 0.32 J/cm | 0.599 ft-lb/in | -40?C; 50%RH; ASTM D 256 | |
| Izod Impact, Notched | 0.43 J/cm | 0.806 ft-lb/in | -40?C; DAM; ASTM D 256 | |
| Izod Impact, Notched | 0.43 J/cm | 0.806 ft-lb/in | DAM; ASTM D 256 | |
| Izod Impact, Notched | 0.75 J/cm | 1.41 ft-lb/in | 50%RH; ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | 1e+011 ohm-cm | 1e+011 ohm-cm | 50%RH; IEC 60093 | |
| Volume Resistivity | 1e+013 ohm-cm | 1e+013 ohm-cm | 50%RH; ASTM D 257 | |
| Volume Resistivity | 1e+013 ohm-cm | 1e+013 ohm-cm | DAM; IEC 60093 | |
| Volume Resistivity | 1e+014 ohm-cm | 1e+014 ohm-cm | DAM; ASTM D 257 | |
| Surface Resistance | 1e+012 ohm | 1e+012 ohm | 50%RH; IEC 60093 | |
| Surface Resistance | 1e+012 ohm | 1e+012 ohm | DAM; IEC 60093 | |
| Surface Resistance | 1e+014 ohm | 1e+014 ohm | 50%RH; ASTM D 257 | |
| Surface Resistance | 1e+015 ohm | 1e+015 ohm | DAM; ASTM D 257 | |
| Dielectric Constant | 3.2 | 3.2 | 1E6 Hz; 23?C; DAM; IEC 60250 | |
| Dielectric Constant | 3.4 | 3.4 | 1E6 Hz; 23?C; 50%RH; IEC 60250 | |
| Dielectric Constant | 3.6 | 3.6 | 1E2 Hz; 23?C; DAM; IEC 60250 | |
| Dielectric Constant | 5.3 | 5.3 | 1E2 Hz; 23?C; 50%RH; IEC 60250 | |
| Dielectric Strength | 21.7 kV/mm | 551 kV/in | 50%RH; 2.0mm; IEC 60243-1 | |
| Dielectric Strength | 22.6 kV/mm | 574 kV/in | DAM; 2.0mm; IEC 60243-1 | |
| Dissipation Factor | 0.014 | 0.014 | DAM; 1E2 Hz; IEC 60250 | |
| Dissipation Factor | 0.016 | 0.016 | DAM; 1E6 Hz; IEC 60250 | |
| Dissipation Factor | 0.02 | 0.02 | DAM; 1E6 Hz; ASTM D 150 | |
| Dissipation Factor | 0.02 | 0.02 | DAM; 1E3 Hz; ASTM D 150 | |
| Dissipation Factor | 0.02 | 0.02 | DAM; 1E2 Hz; ASTM D 150 | |
| Dissipation Factor | 0.04 | 0.04 | 50%RH; 1E6 Hz; IEC 60250 | |
| Dissipation Factor | 0.1 | 0.1 | 50%RH; 1E2 Hz; IEC 60250 | |
| Comparative Tracking Index | Min 600 V | Min 600 V | DAM; UL 746A | |
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 120 ?m/m-?C | 66.7 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C | 90 ?m/m-?C | 50 ?in/in-?F | DAM; -40 - 23?C (-40 - 73?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 120 ?m/m-?C | 66.7 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 180 ?m/m-?C | 100 ?in/in-?F | DAM; 55 - 160?C (130 - 320?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 90 ?m/m-?C | 50 ?in/in-?F | DAM; -40 - 23?C (-40 - 73?F); ISO 11359-1/-2 | |
| CTE, linear 100?C | 170 ?m/m-?C | 94.4 ?in/in-?F | DAM; 55 - 160?C (130 - 320?F); Parallel; ISO 11359-1/-2 | |
| Melting Point | 218 ?C | 424 ?F | DAM; ASTM D 3418 | |
| Melting Point | 218 ?C | 424 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 ?C | 275 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55 ?C | 131 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 62 ?C | 144 ?F | DAM; ISO 75-1/-2 | |
| Brittleness Temperature | -109 ?C | -164 ?F | 50%RH; ASTM D 746 | |
| Brittleness Temperature | -126 ?C | -195 ?F | DAM; ASTM D 746 | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 0.86mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 0.86mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 0.86mm; DAM; UL 746B | |
| Flammability, UL94 | HB | HB | 0.86mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 0.86mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; IEC 60695-11-10 | |
| Oxygen Index | 27 % | 27 % | DAM; ISO 4589-1/-2 | |
| Glow Wire Test | 675 ?C | 1250 ?F | 1.5mm; DAM; Flammability Index; IEC 60695-2-12 | |
| Glow Wire Test | 675 ?C | 1250 ?F | 0.86mm; DAM; Ignition Temperature; IEC 60695-2-13 | |
| Glow Wire Test | 675 ?C | 1250 ?F | 1.5mm; DAM; Ignition Temperature; IEC 60695-2-13 | |
| Glow Wire Test | 700 ?C | 1290 ?F | 3.0mm; DAM; Ignition Temperature; IEC 60695-2-13 | |
| Glow Wire Test | 825 ?C | 1520 ?F | 0.86mm; DAM; Flammability Index; IEC 60695-2-12 | |
| Glow Wire Test | 925 ?C | 1700 ?F | 3.0mm; DAM; Flammability Index; IEC 60695-2-12 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 230 - 290 ?C | 446 - 554 ?F | ||
| Melt Temperature | 250 ?C | 482 ?F | Optimum | |
| Mold Temperature | 50 - 90 ?C | 122 - 194 ?F | ||
| Mold Temperature | 70 ?C | 158 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.15 % | Max 0.15 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Heat Stabilizer | |||
| Additive | Lubricant | |||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Extrusion Resins | |||
| DuPont Product Category | Unreinforced Resins | |||
| Extrudable | Blown Film | |||
| Extrudable | Coating | |||
| Extrudable | Filament | |||
| Extrudable | Hose | |||
| Extrudable | Sheet | |||
| Extrudable | Tubing | |||
| Extrudable | Wire and Cable | |||
| Extrusion Blow Moldable | Yes | |||
| Features | Chemical Resistance, Good | |||
| Features | Electrical Properties, Good | |||
| Features | Heat Aging Resistance, Good | |||
| Form | Pellets | |||
| Heat Stabilized | Yes | |||
| Injection Blow Moldable | Yes | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >PA612< | ISO 11469 | ||
| Processing Method | Extrusion | |||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA612 | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Automotive Applications | |||
| Uses | Cable Jacketing | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.