DuPont Zytel? 157HSL BK010 Nylon 612
Subcategory: Nylon; Nylon 612; Polymer; Thermoplastic
Material Notes:
Zytel? 157HSL BK010 is a heat stabilized, weatherable, lubricated polyamide 612 resin that is suitable for molding and extrusion applications.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.07 g/cc | 0.0387 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.07 g/cc | 0.0387 lb/in? | DAM; ASTM D 792 | |
| Water Absorption | 0.3 % | 0.3 % | Immersion 24h; 23?C; DAM; ASTM D 570 | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 2.0mm; ISO 294-4 | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell R | 120 | 120 | DAM; ASTM D 785 | |
| Tensile Strength, Ultimate | 55 MPa | 7980 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Ultimate | 60 MPa | 8700 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 53 MPa | 7690 psi | 50%RH; ISO 527 | |
| Tensile Strength, Yield | 65 MPa | 9430 psi | DAM; ISO 527 | |
| Elongation at Break | Min 50 % | Min 50 % | 50%RH; Nominal; ISO 527 | |
| Elongation at Break | 22 % | 22 % | DAM; Nominal; ISO 527 | |
| Elongation at Break | 30 % | 30 % | DAM; ASTM D 638 | |
| Elongation at Break | 75 % | 75 % | 50%RH; ASTM D 638 | |
| Elongation at Yield | 18 % | 18 % | ISO 527 | |
| Elongation at Yield | 4.4 % | 4.4 % | ISO 527 | |
| Tensile Modulus | 1.5 GPa | 218 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 2.5 GPa | 363 ksi | DAM; ISO 527 | |
| Flexural Modulus | 1.5 GPa | 218 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 1.5 GPa | 218 ksi | 50%RH; ISO 178 | |
| Flexural Modulus | 2.18 GPa | 316 ksi | DAM; ASTM D 790 | |
| Flexural Modulus | 2.3 GPa | 334 ksi | DAM; ISO 178 | |
| Flexural Strength | 44 MPa | 6380 psi | 50%RH; ISO 178 | |
| Flexural Strength | 80 MPa | 11600 psi | DAM; ISO 178 | |
| Izod Impact, Notched (ISO) | 4 kJ/m? | 1.9 ft-lb/in? | DAM; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.4 J/cm? | 1.9 ft-lb/in? | DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 0.7 J/cm? | 3.33 ft-lb/in? | 50%RH; ISO 179/1eA | |
| Izod Impact, Notched | 0.43 J/cm | 0.806 ft-lb/in | DAM; ASTM D 256 | |
| Izod Impact, Notched | 0.48 J/cm | 0.899 ft-lb/in | 50%RH; ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Comparative Tracking Index | Min 600 V | Min 600 V | DAM; UL 746A | |
Thermal Properties |
||||
|
||||
| Melting Point | 218 ?C | 424 ?F | DAM; ASTM D 3418 | |
| Melting Point | 218 ?C | 424 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 ?C | 302 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50 ?C | 122 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 62 ?C | 144 ?F | DAM; ISO 75-1/-2 | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 0.86mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 0.86mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 0.86mm; DAM; UL94 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 230 - 290 ?C | 446 - 554 ?F | ||
| Melt Temperature | 250 ?C | 482 ?F | Optimum | |
| Mold Temperature | 50 - 90 ?C | 122 - 194 ?F | ||
| Mold Temperature | 70 ?C | 158 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.05 % | Max 0.05 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Heat Stabilizer | |||
| Additive | Carbon Black | |||
| Additive | Lubricant | |||
| Appearance | Black | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | UV Resistant/Weatherable Resins | |||
| DuPont Product Category | Unreinforced Resins | |||
| DuPont Product Category | Extrusion Resins | |||
| Extrudable | Blown Film | |||
| Extrudable | Coating | |||
| Extrudable | Filament | |||
| Extrudable | Hose | |||
| Extrudable | Sheet | |||
| Extrudable | Tubing | |||
| Extrudable | Wire and Cable | |||
| Extrusion Blow Moldable | Yes | |||
| Features | Lubricated | |||
| Features | Heat Aging Resistance, Good | |||
| Features | Chemical Resistance, Good | |||
| Features | Weather Resistance, Good | |||
| Form | Pellets | |||
| Heat Stabilized | Yes | |||
| Injection Blow Moldable | Yes | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >PA612< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA612 | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Automotive Applications | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.