DuPont Zytel? 350PHS2 NC010 Nylon 612
Subcategory: Nylon; Nylon 612; Polymer; Thermoplastic
Material Notes:
Zytel? 350PHS2 NC010 is a flexible, tough, low moisture absorption polyamide 612 resin for extrusion applications; e.g. fuel lines, hose liners, and tubing requiring chemical resistance and flexibility.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.02 g/cc | 0.0368 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.03 g/cc | 0.0372 lb/in? | DAM; ASTM D 792 | |
| Water Absorption | 0.28 % | 0.28 % | Immersion 24h; 23?C; DAM; ASTM D 570 | |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | Flow 3.2mm (0.125in) | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 3.2mm (0.125in) | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell R | 87 | 87 | DAM; ASTM D 785 | |
| Tensile Strength, Ultimate | 37.1 MPa | 5380 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Ultimate | 41 MPa | 5950 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 28 MPa | 4060 psi | DAM; ISO 527 | |
| Elongation at Break | Min 50 % | Min 50 % | DAM; Nominal; ISO 527 | |
| Elongation at Break | 200 % | 200 % | DAM; Nominal; ISO 527 | |
| Elongation at Break | 250 % | 250 % | ISO 527 | |
| Elongation at Break | 304 % | 304 % | 50%RH; ASTM D 638 | |
| Elongation at Break | 329 % | 329 % | DAM; ASTM D 638 | |
| Elongation at Yield | 35 % | 35 % | ISO 527 | |
| Tensile Modulus | 0.8 GPa | 116 ksi | DAM; ISO 527 | |
| Flexural Modulus | 0.524 GPa | 76 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 0.67 GPa | 97.2 ksi | DAM; ISO 178 | |
| Flexural Modulus | 0.828 GPa | 120 ksi | DAM; ASTM D 790 | |
| Flexural Strength | 18 MPa | 2610 psi | 50%RH; ASTM D 790 | |
| Flexural Strength | 29 MPa | 4210 psi | DAM; ASTM D 790 | |
| Izod Impact, Notched (ISO) | 60 kJ/m? | 28.6 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 12 kJ/m? | 5.71 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Charpy Impact, Notched | 7 J/cm? | 33.3 ft-lb/in? | DAM; ISO 179/1eA | |
| Izod Impact, Notched | 1.356 J/cm | 2.54 ft-lb/in | -40?C; DAM; ASTM D 256 | |
| Izod Impact, Notched | 8.294 J/cm | 15.5 ft-lb/in | DAM; ASTM D 256 | |
Thermal Properties |
||||
|
||||
| Melting Point | 214 ?C | 417 ?F | DAM; ASTM D 3418 | |
| Melting Point | 215 ?C | 419 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 ?C | 248 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 43 ?C | 109 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 45 ?C | 113 ?F | DAM; ISO 75-1/-2 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 230 - 290 ?C | 446 - 554 ?F | ||
| Melt Temperature | 250 ?C | 482 ?F | Optimum | |
| Mold Temperature | 50 - 90 ?C | 122 - 194 ?F | ||
| Mold Temperature | 70 ?C | 158 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.05 % | Max 0.05 % | ||
Descriptive Properties |
||||
|
||||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Toughened Resins | |||
| DuPont Product Category | Extrusion Resins | |||
| DuPont Product Category | Unreinforced Resins | |||
| Form | Pellets | |||
| Part Marking Code | >PA612-HIP< | ISO 11469 | ||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA612-HIP | ISO 1043 | ||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.