DuPont Zytel? 77G33HS1L NC010 Nylon 612
Subcategory: Nylon; Nylon 612; Polymer; Thermoplastic
Material Notes:
Zytel? 77G33HS1L NC010 is a 33% glass fiber reinforced, heat stabilized polyamide 612 resin for injection molding.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.32 g/cc | 0.0477 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.32 g/cc | 0.0477 lb/in? | DAM; ASTM D 792 | |
| Filler Content | 33 % | 33 % | Glass fiber reinforcement | |
| Water Absorption | 0.16 % | 0.16 % | Immersion 24h; 23?C; DAM; ASTM D 570 | |
| Water Absorption at Saturation | 2 % | 2 % | DAM; ASTM D 570 | |
| Linear Mold Shrinkage | 0.001 cm/cm | 0.001 in/in | Flow 1.6mm (0.062in) | |
| Linear Mold Shrinkage | 0.002 cm/cm | 0.002 in/in | Flow 3.2mm (0.125in) | |
| Linear Mold Shrinkage | 0.003 cm/cm | 0.003 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage | 0.004 cm/cm | 0.004 in/in | Flow 6.4mm (0.25in) | |
| Linear Mold Shrinkage, Transverse | 0.009 cm/cm | 0.009 in/in | 1.6mm (0.062in) | |
| Linear Mold Shrinkage, Transverse | 0.009 cm/cm | 0.009 in/in | 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.01 cm/cm | 0.01 in/in | 3.2mm (0.125in) | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | 6.4mm (0.25in) | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell R | 118 | 118 | DAM; ASTM D 785 | |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | 50%RH; ASTM D 638 | |
| Tensile Strength at Break | 140 MPa | 20300 psi | 50%RH; ISO 527 | |
| Tensile Strength, Ultimate | 165 MPa | 23900 psi | DAM; ASTM D 638 | |
| Tensile Strength at Break | 168 MPa | 24400 psi | DAM; ISO 527 | |
| Elongation at Break | 3 % | 3 % | DAM; ASTM D 638 | |
| Elongation at Break | 3 % | 3 % | ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527 | |
| Elongation at Break | 4 % | 4 % | 50%RH; ASTM D 638 | |
| Tensile Modulus | 7.9 GPa | 1150 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 9.5 GPa | 1380 ksi | DAM; ISO 527 | |
| Flexural Modulus | 6.2 GPa | 899 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 7 GPa | 1020 ksi | 50%RH; ISO 178 | |
| Flexural Modulus | 8.2 GPa | 1190 ksi | DAM; ISO 178 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | DAM; ASTM D 790 | |
| Flexural Strength | 255 MPa | 37000 psi | DAM; ASTM D 790 | |
| Shear Strength | 76 MPa | 11000 psi | DAM; ASTM D 732 | |
| Izod Impact, Notched (ISO) | 12 kJ/m? | 5.71 ft-lb/in? | 50%RH; ISO 180/1A | |
| Izod Impact, Notched (ISO) | 13 kJ/m? | 6.19 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 60 kJ/m? | 28.6 ft-lb/in? | 50%RH; ISO 180/1U | |
| Izod Impact, Unnotched (ISO) | 70 kJ/m? | 33.3 ft-lb/in? | DAM; ISO 180/1U | |
| Izod Impact, Unnotched Low Temp (ISO) | 45 kJ/m? | 21.4 ft-lb/in? | -30?C; 50%RH; ISO 180/1U | |
| Izod Impact, Unnotched Low Temp (ISO) | 60 kJ/m? | 28.6 ft-lb/in? | -30?C; DAM; ISO 180/1U | |
| Izod Impact, Notched, Low Temp (ISO) | 10 kJ/m? | 4.76 ft-lb/in? | -30?C; 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 10 kJ/m? | 4.76 ft-lb/in? | -40?C; 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | -30?C; DAM; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | 8 J/cm? | 38.1 ft-lb/in? | DAM; ISO 179/1eU | |
| Charpy Impact Unnotched | 9 J/cm? | 42.8 ft-lb/in? | 50%RH; ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 1 J/cm? | 4.76 ft-lb/in? | -30?C; 50%RH; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 1 J/cm? | 4.76 ft-lb/in? | -40?C; 50%RH; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 1.1 J/cm? | 5.24 ft-lb/in? | -30?C; DAM; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 1.2 J/cm? | 5.71 ft-lb/in? | -40?C; DAM; ISO 179/1eA | |
| Charpy Impact, Unnotched Low Temp | 6 J/cm? | 28.6 ft-lb/in? | -30?C; DAM; ISO 179/1eU | |
| Charpy Impact, Unnotched Low Temp | 6.5 J/cm? | 30.9 ft-lb/in? | -30?C; 50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 1.2 J/cm? | 5.71 ft-lb/in? | 50%RH; ISO 179/1eA | |
| Charpy Impact, Notched | 1.3 J/cm? | 6.19 ft-lb/in? | DAM; ISO 179/1eA | |
| Izod Impact, Notched | 1.28 J/cm | 2.4 ft-lb/in | DAM; ASTM D 256 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | 50%RH; ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | 1e+012 ohm-cm | 1e+012 ohm-cm | 50%RH; ASTM D 257 | |
| Volume Resistivity | 1e+013 ohm-cm | 1e+013 ohm-cm | DAM; IEC 60093 | |
| Volume Resistivity | 1e+015 ohm-cm | 1e+015 ohm-cm | DAM; ASTM D 257 | |
| Surface Resistance | 1e+015 ohm | 1e+015 ohm | DAM; ASTM D 257 | |
| Dielectric Constant | 3.4 | 3.4 | DAM; 1E6 Hz; ASTM D 150 | |
| Dielectric Constant | 3.7 | 3.7 | DAM; 1E3 Hz; ASTM D 150 | |
| Dielectric Strength | 20.5 kV/mm | 521 kV/in | 23?C; 3.2mm (0.125in); DAM; Short Time; ASTM D 149 | |
| Dissipation Factor | 0.02 | 0.02 | DAM; 1E3 Hz; ASTM D 150 | |
| Dissipation Factor | 0.02 | 0.02 | DAM; 1E6 Hz; ASTM D 150 | |
| Comparative Tracking Index | Min 550 V | Min 550 V | DAM; UL 746A | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 17 ?m/m-?C | 9.44 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 17 ?m/m-?C | 9.44 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C | 26 ?m/m-?C | 14.4 ?in/in-?F | DAM; -40 - 23?C (-40 - 73?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 26 ?m/m-?C | 14.4 ?in/in-?F | DAM; -40 - 23?C (-40 - 73?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 113 ?m/m-?C | 62.8 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 113 ?m/m-?C | 62.8 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 158 ?m/m-?C | 87.8 ?in/in-?F | DAM; 55 - 160?C (130 - 320?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 158 ?m/m-?C | 87.8 ?in/in-?F | DAM; 55 - 160?C (130 - 320?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 83 ?m/m-?C | 46.1 ?in/in-?F | DAM; -40 - 23?C (-40 - 73?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 83 ?m/m-?C | 46.1 ?in/in-?F | DAM; -40 - 23?C (-40 - 73?F); ISO 11359-1/-2 | |
| CTE, linear 100?C | 16 ?m/m-?C | 8.89 ?in/in-?F | DAM; 55 - 160?C (130 - 320?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 100?C | 16 ?m/m-?C | 8.89 ?in/in-?F | DAM; 55 - 160?C (130 - 320?F); Parallel; ASTM E 831 | |
| Melting Point | 217 ?C | 423 ?F | DAM; ASTM D 3418 | |
| Melting Point | 218 ?C | 424 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 ?C | 421 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 ?C | 392 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 ?C | 410 ?F | DAM; ASTM D 648 | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 0.75mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 0.75mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 0.75mm; DAM; UL 746B | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 0.75mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 0.75mm; DAM; UL94 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 280 - 300 ?C | 536 - 572 ?F | ||
| Melt Temperature | 290 ?C | 554 ?F | Optimum | |
| Mold Temperature | 70 - 120 ?C | 158 - 248 ?F | ||
| Mold Temperature | 100 ?C | 212 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.15 % | Max 0.15 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Heat Stabilizer | |||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Glass Reinforced Resins | |||
| Features | Heat Stabilized | |||
| Features | Dimensional Stability, Good | |||
| Features | Moisture Absorption, Low | |||
| Form | Pellets | |||
| Heat Stabilized | Yes | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >PA612-GF33< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Resin Identification | PA612-GF33 | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Appliance Components | |||
| Uses | Electrical/Electronic Applications | |||
| Uses | Industrial Applications | |||
| Uses | Automotive Applications | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.