DuPont Zytel? FE5382 BK276 Nylon 612
Subcategory: Nylon; Nylon 612; Polymer; Thermoplastic
Material Notes:
Zytel? FE5382 BK276 is a 33% glass fiber reinforced, heat stabilized, black polyamide 612 resin developed for electrical bobbins and encapsulation applications.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.32 g/cc | 0.0477 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.32 g/cc | 0.0477 lb/in? | DAM; ASTM D 792 | |
| Filler Content | 33 % | 33 % | Glass fiber reinforcement | |
| Linear Mold Shrinkage | 0.003 cm/cm | 0.003 in/in | Flow 3.2mm (0.125in) | |
| Linear Mold Shrinkage, Transverse | 0.01 cm/cm | 0.01 in/in | 3.2mm (0.125in) | |
Mechanical Properties |
||||
|
||||
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Ultimate | 165 MPa | 23900 psi | DAM; ASTM D 638 | |
| Tensile Strength at Break | 170 MPa | 24700 psi | DAM; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | DAM; ASTM D 638 | |
| Elongation at Break | 3 % | 3 % | 50%RH; ASTM D 638 | |
| Tensile Modulus | 9.8 GPa | 1420 ksi | DAM; ISO 527 | |
| Flexural Modulus | 6.205 GPa | 900 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 8.4 GPa | 1220 ksi | DAM; ISO 178 | |
| Flexural Modulus | 8.965 GPa | 1300 ksi | DAM; ASTM D 790 | |
| Flexural Strength | 193 MPa | 28000 psi | 50%RH; ASTM D 790 | |
| Flexural Strength | 248 MPa | 36000 psi | DAM; ASTM D 790 | |
| Izod Impact, Notched (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Unnotched | 9.6 J/cm | 18 ft-lb/in | ASTM D 4812 | |
| Izod Impact, Unnotched | 9.6 J/cm | 18 ft-lb/in | ASTM D 4812 | |
| Izod Impact, Notched, Low Temp (ISO) | 10 kJ/m? | 4.76 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Charpy Impact, Notched, Low Temp | 1 J/cm? | 4.76 ft-lb/in? | -40?C; DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 1.2 J/cm? | 5.71 ft-lb/in? | DAM; ISO 179/1eA | |
| Izod Impact, Notched | 1.07 J/cm | 2 ft-lb/in | 50%RH; ASTM D 256 | |
| Izod Impact, Notched | 1.07 J/cm | 2 ft-lb/in | DAM; ASTM D 256 | |
Thermal Properties |
||||
|
||||
| Melting Point | 218 ?C | 424 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Melting Point | 219 ?C | 426 ?F | DAM; ASTM D 3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 ?C | 401 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 ?C | 392 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 ?C | 392 ?F | DAM; ASTM D 648 | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 0.75mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 0.75mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 0.75mm; DAM; UL 746B | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 0.75mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 0.75mm; DAM; UL94 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 280 - 300 ?C | 536 - 572 ?F | ||
| Melt Temperature | 290 ?C | 554 ?F | Optimum | |
| Mold Temperature | 70 - 120 ?C | 158 - 248 ?F | ||
| Mold Temperature | 100 ?C | 212 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.15 % | Max 0.15 % | ||
Descriptive Properties |
||||
|
||||
| Appearance | Black | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Encapsulation Resins | |||
| DuPont Product Category | Glass Reinforced Resins | |||
| Form | Pellets | |||
| Part Marking Code | >PA612-GF33< | ISO 11469 | ||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA612-GF33 | ISO 1043 | ||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.