DuPont Zytel? 73G15THSL BK240 Nylon 6
Subcategory: Nylon; Nylon 6; Polymer; Thermoplastic
Material Notes:
Zytel? 73G15THSL BK240 is a 15% glass fiber reinforced, toughened, heat stabilized, black polyamide 6 resin for injection molding.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.2 g/cc | 0.0434 lb/in? | DAM; ISO 1183 | |
| Filler Content | 15 % | 15 % | Glass fiber reinforcement | |
| Linear Mold Shrinkage | 0.002 cm/cm | 0.002 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.006 cm/cm | 0.006 in/in | 2.0mm; ISO 294-4 | |
Mechanical Properties |
||||
|
||||
| Tensile Strength at Break | 110 MPa | 16000 psi | DAM; ISO 527 | |
| Tensile Strength at Break | 55 MPa | 7980 psi | 50%RH; ISO 527 | |
| Elongation at Break | 3 % | 3 % | ISO 527 | |
| Elongation at Break | 7 % | 7 % | ISO 527 | |
| Tensile Modulus | 3.2 GPa | 464 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 5.5 GPa | 798 ksi | DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 10 kJ/m? | 4.76 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Notched (ISO) | 13 kJ/m? | 6.19 ft-lb/in? | 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 5 kJ/m? | 2.38 ft-lb/in? | -30?C; 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 5 kJ/m? | 2.38 ft-lb/in? | -30?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | 6 J/cm? | 28.6 ft-lb/in? | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | 6 J/cm? | 28.6 ft-lb/in? | DAM; ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 0.5 J/cm? | 2.38 ft-lb/in? | -30?C; DAM; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 0.5 J/cm? | 2.38 ft-lb/in? | -30?C; 50%RH; ISO 179/1eA | |
| Charpy Impact, Notched | 1 J/cm? | 4.76 ft-lb/in? | DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 1.3 J/cm? | 6.19 ft-lb/in? | 50%RH; ISO 179/1eA | |
Thermal Properties |
||||
|
||||
| Melting Point | 221 ?C | 430 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 ?C | 392 ?F | DAM; ISO 75-1/-2 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 260 - 280 ?C | 500 - 536 ?F | ||
| Melt Temperature | 270 ?C | 518 ?F | Optimum | |
| Mold Temperature | 50 - 100 ?C | 122 - 212 ?F | ||
| Mold Temperature | 80 ?C | 176 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | ||
Descriptive Properties |
||||
|
||||
| Appearance | Black | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Glass Reinforced Resins | |||
| DuPont Product Category | Toughened Resins | |||
| Form | Pellets | |||
| Heat Stabilized | Yes | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >PA6-IGF15< | ISO 11469 | ||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA6-IGF15 | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.