DuPont Zytel? 73G30HSL BK416 Nylon 6
Subcategory: Nylon; Nylon 6; Polymer; Thermoplastic
Material Notes:
Zytel? 73G30HSL BK416 is a 30% glass fiber reinforced, heat stabilized, black polyamide 6 resin for injection molding.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.36 g/cc | 0.0491 lb/in? | DAM; ISO 1183 | |
| Filler Content | 30 % | 30 % | Glass fiber reinforcement | |
| Linear Mold Shrinkage | 0.001 cm/cm | 0.001 in/in | Flow 1.6mm (0.062in) | |
| Linear Mold Shrinkage | 0.002 cm/cm | 0.002 in/in | Flow 3.2mm (0.125in) | |
| Linear Mold Shrinkage | 0.002 cm/cm | 0.002 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage | 0.003 cm/cm | 0.003 in/in | Flow 6.4mm (0.25in) | |
| Linear Mold Shrinkage, Transverse | 0.006 cm/cm | 0.006 in/in | 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.007 cm/cm | 0.007 in/in | 1.6mm (0.062in) | |
| Linear Mold Shrinkage, Transverse | 0.008 cm/cm | 0.008 in/in | 3.2mm (0.125in) | |
| Linear Mold Shrinkage, Transverse | 0.008 cm/cm | 0.008 in/in | 6.4mm (0.25in) | |
Mechanical Properties |
||||
|
||||
| Tensile Strength at Break | 115 MPa | 16700 psi | 50%RH; ISO 527 | |
| Tensile Strength at Break | 190 MPa | 27600 psi | DAM; ISO 527 | |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 | |
| Elongation at Break | 6 % | 6 % | ISO 527 | |
| Tensile Modulus | 5.8 GPa | 841 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 9.8 GPa | 1420 ksi | DAM; ISO 527 | |
| Flexural Modulus | 8.2 GPa | 1190 ksi | DAM; ISO 178 | |
| Izod Impact, Notched (ISO) | 15 kJ/m? | 7.14 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Notched (ISO) | 20 kJ/m? | 9.52 ft-lb/in? | 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | 9.5 J/cm? | 45.2 ft-lb/in? | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | 9.5 J/cm? | 45.2 ft-lb/in? | DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 1.6 J/cm? | 7.61 ft-lb/in? | DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 2.3 J/cm? | 10.9 ft-lb/in? | 50%RH; ISO 179/1eA | |
Thermal Properties |
||||
|
||||
| Melting Point | 221 ?C | 430 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 ?C | 428 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 ?C | 399 ?F | DAM; ISO 75-1/-2 | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 0.8mm; DAM; UL 746B | |
| UL RTI, Electrical | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 0.8mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 65 ?C | 149 ?F | 0.8mm; DAM; UL 746B | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 1.5mm; DAM; UL94 | |
| Flammability, UL94 | HB | HB | 0.8mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 0.8mm; DAM; UL94 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 260 - 280 ?C | 500 - 536 ?F | ||
| Melt Temperature | 270 ?C | 518 ?F | Optimum | |
| Mold Temperature | 70 - 120 ?C | 158 - 248 ?F | ||
| Mold Temperature | 100 ?C | 212 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Heat Stabilizer | |||
| Additive | Lubricant | |||
| Appearance | Black | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Glass Reinforced Resins | |||
| Features | Weather Resistance, Good | |||
| Form | Pellets | |||
| Heat Stabilized | Yes | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >PA6-GF30< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA6-GF30 | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Parts, Engineering | |||
| Uses | Parts, Machine/Mechanical | |||
| Uses | Automotive Applications | |||
| Uses | Appliance Components | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.