DuPont Zytel? 73G30HSL NC010 Nylon 6
Subcategory: Nylon; Nylon 6; Polymer; Thermoplastic
Material Notes:
Zytel? 73G30HSL NC010 is a 30% glass fiber reinforced, heat stabilized polyamide 6 resin for injection molding.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.36 g/cc | 0.0491 lb/in? | DAM; ISO 1183 | |
| Filler Content | 30 % | 30 % | Glass fiber reinforcement | |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50%RH; 23?C; DAM; ISO 62, Similar to | |
| Water Absorption at Saturation | 6.3 % | 6.3 % | Immersed; 23?C; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage | 0.002 cm/cm | 0.002 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.006 cm/cm | 0.006 in/in | 2.0mm; ISO 294-4 | |
Mechanical Properties |
||||
|
||||
| Tensile Strength at Break | 115 MPa | 16700 psi | 50%RH; ISO 527 | |
| Tensile Strength at Break | 185 MPa | 26800 psi | DAM; ISO 527 | |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 | |
| Elongation at Break | 6 % | 6 % | ISO 527 | |
| Tensile Modulus | 5.8 GPa | 841 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 9.7 GPa | 1410 ksi | DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 15 kJ/m? | 7.14 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Notched (ISO) | 20 kJ/m? | 9.52 ft-lb/in? | 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 10 kJ/m? | 4.76 ft-lb/in? | -30?C; DAM; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | -30?C; 50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 10 J/cm? | 47.6 ft-lb/in? | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | 10 J/cm? | 47.6 ft-lb/in? | DAM; ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 1 J/cm? | 4.76 ft-lb/in? | -30?C; DAM; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 2.1 J/cm? | 9.99 ft-lb/in? | -30?C; 50%RH; ISO 179/1eA | |
| Charpy Impact, Unnotched Low Temp | 8 J/cm? | 38.1 ft-lb/in? | -30?C; DAM; ISO 179/1eU | |
| Charpy Impact, Unnotched Low Temp | 8.4 J/cm? | 40 ft-lb/in? | -30?C; 50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 1.6 J/cm? | 7.61 ft-lb/in? | DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 2.3 J/cm? | 10.9 ft-lb/in? | 50%RH; ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 6190 MPa | 898000 psi | 50%RH; ISO 899 | |
| Tensile Creep Modulus, 1000 hours | 4630 MPa | 672000 psi | 50%RH; ISO 899 | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 22 ?m/m-?C | 12.2 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 22 ?m/m-?C | 12.2 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 102 ?m/m-?C | 56.7 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 102 ?m/m-?C | 56.7 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| Melting Point | 221 ?C | 430 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 ?C | 428 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 ?C | 410 ?F | DAM; ISO 75-1/-2 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 260 - 280 ?C | 500 - 536 ?F | ||
| Melt Temperature | 270 ?C | 518 ?F | Optimum | |
| Mold Temperature | 70 - 120 ?C | 158 - 248 ?F | ||
| Mold Temperature | 100 ?C | 212 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Heat Stabilizer | |||
| Additive | Lubricant | |||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Glass Reinforced Resins | |||
| Features | Thermal Aging Resistance, Good | |||
| Features | Oil Resistant | |||
| Features | Heat Aging Resistance, Good | |||
| Features | Grease Resistant | |||
| Features | Fuel Resistant | |||
| Features | Chemical Resistance, Good | |||
| Features | Fatigue Resistant | |||
| Form | Pellets | |||
| Part Marking Code | >PA6-GF30< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA6-GF30 | ISO 1043 | ||
| Uses | Electrical/Electronic Applications | |||
| Uses | High Gloss Applications | |||
| Uses | Industrial Applications | |||
| Uses | Appliance Components | |||
| Uses | Automotive Applications | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.