DuPont Zytel? 103FHS NC010 Nylon 66
Subcategory: Nylon; Nylon 66; Polymer; Thermoplastic
Material Notes:
Zytel? 103FHS NC010 is a heat stabilized, internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.14 g/cc | 0.0412 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.14 g/cc | 0.0412 lb/in? | DAM; ASTM D 792 | |
| Water Absorption | 1.2 % | 1.2 % | Immersion 24h; 23?C; DAM; ASTM D 570 | |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 50%RH; 23?C; DAM; ISO 62, Similar to | |
| Water Absorption at Saturation | 8.5 % | 8.5 % | Immersed; 23?C; DAM; ISO 62, Similar to | |
| Water Absorption at Saturation | 8.6 % | 8.6 % | DAM; ASTM D 570 | |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | Flow 1.6mm (0.062in) | |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | Flow 3.2mm (0.125in) | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | 2.0mm; ISO 294-4 | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell R | 121 | 121 | DAM; ASTM D 785 | |
| Tensile Strength, Ultimate | 41 MPa | 5950 psi | 121?C; DAM; ASTM D 638 | |
| Tensile Strength, Ultimate | 55 MPa | 7980 psi | 77?C; DAM; ASTM D 638 | |
| Tensile Strength, Ultimate | 59 MPa | 8560 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Ultimate | 83 MPa | 12000 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 55 MPa | 7980 psi | 50%RH; ISO 527 | |
| Tensile Strength, Yield | 85 MPa | 12300 psi | DAM; ISO 527 | |
| Elongation at Break | Min 50 % | Min 50 % | 50%RH; Nominal; ISO 527 | |
| Elongation at Break | Min 250 % | Min 250 % | 121?C; DAM; ASTM D 638 | |
| Elongation at Break | Min 250 % | Min 250 % | 50%RH; ASTM D 638 | |
| Elongation at Break | Min 100 % | Min 100 % | 50%RH; Nominal; ISO 527 | |
| Elongation at Break | 190 % | 190 % | 77?C; DAM; ASTM D 638 | |
| Elongation at Break | 20 % | 20 % | DAM; Nominal; ISO 527 | |
| Elongation at Break | 50 % | 50 % | DAM; ASTM D 638 | |
| Elongation at Yield | 25 % | 25 % | ISO 527 | |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527 | |
| Tensile Modulus | 1.4 GPa | 203 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 3.1 GPa | 450 ksi | DAM; ISO 527 | |
| Flexural Modulus | 0.414 GPa | 60 ksi | 130?C; DAM; ASTM D 790 | |
| Flexural Modulus | 0.415 GPa | 60.2 ksi | 121?C; 50%RH; ASTM D 790 | |
| Flexural Modulus | 0.538 GPa | 78 ksi | 121?C; DAM; ASTM D 790 | |
| Flexural Modulus | 0.565 GPa | 81.9 ksi | 77?C; 50%RH; ASTM D 790 | |
| Flexural Modulus | 1.1 GPa | 160 ksi | 77?C; DAM; ASTM D 790 | |
| Flexural Modulus | 1.21 GPa | 175 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 1.3 GPa | 189 ksi | 50%RH; ISO 178 | |
| Flexural Modulus | 2.8 GPa | 406 ksi | DAM; ISO 178 | |
| Flexural Modulus | 2.83 GPa | 410 ksi | DAM; ASTM D 790 | |
| Shear Strength | 65 MPa | 9430 psi | 50%RH; ASTM D 732 | |
| Shear Strength | 73.8 MPa | 10700 psi | DAM; ASTM D 732 | |
| Izod Impact, Notched (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | 50%RH; ISO 180/1A | |
| Izod Impact, Notched (ISO) | 5.5 kJ/m? | 2.62 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 300 kJ/m? | 143 ft-lb/in? | DAM; ISO 180/1U | |
| Izod Impact, Unnotched (ISO) | NB | NB | 50%RH; ISO 180/1U | |
| Izod Impact, Unnotched Low Temp (ISO) | 300 kJ/m? | 143 ft-lb/in? | -30?C; DAM; ISO 180/1U | |
| Izod Impact, Unnotched Low Temp (ISO) | NB | NB | -30?C; 50%RH; ISO 180/1U | |
| Izod Impact, Notched, Low Temp (ISO) | 5 kJ/m? | 2.38 ft-lb/in? | -30?C; 50%RH; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 5.5 kJ/m? | 2.62 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Izod Impact, Notched, Low Temp (ISO) | 6 kJ/m? | 2.86 ft-lb/in? | -30?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 0.3 J/cm? | 1.43 ft-lb/in? | -40?C; DAM; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 0.3 J/cm? | 1.43 ft-lb/in? | -30?C; 50%RH; ISO 179/1eA | |
| Charpy Impact, Notched, Low Temp | 0.45 J/cm? | 2.14 ft-lb/in? | -30?C; DAM; ISO 179/1eA | |
| Charpy Impact, Unnotched Low Temp | 35 J/cm? | 167 ft-lb/in? | -30?C; DAM; ISO 179/1eU | |
| Charpy Impact, Unnotched Low Temp | NB | NB | -30?C; 50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 0.55 J/cm? | 2.62 ft-lb/in? | DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 1.1 J/cm? | 5.24 ft-lb/in? | 50%RH; ISO 179/1eA | |
| Tensile Impact Strength | 440 kJ/m? | 209 ft-lb/in? | 23?C; Long specimen; DAM; ASTM D 1822 | |
| Tensile Impact Strength | 510 kJ/m? | 243 ft-lb/in? | 121?C; Long specimen; DAM; ASTM D 1822 | |
| Tensile Impact Strength | NB | NB | 121?C; Long specimen; 50%RH; ASTM D 1822 | |
| Izod Impact, Notched | 1.3 J/cm | 2.44 ft-lb/in | 77?C; DAM; ASTM D 256 | |
| Izod Impact, Notched | 1.9 J/cm | 3.56 ft-lb/in | 77?C; 50%RH; ASTM D 256 | |
| Izod Impact, Notched | 0.53 J/cm | 0.993 ft-lb/in | DAM; ASTM D 256 | |
| Izod Impact, Notched | 0.8 J/cm | 1.5 ft-lb/in | 50%RH; ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | 1e+011 ohm-cm | 1e+011 ohm-cm | 50%RH; ASTM D 257 | |
| Volume Resistivity | 1e+014 ohm-cm | 1e+014 ohm-cm | DAM; ASTM D 257 | |
| Dielectric Constant | 3.2 | 3.2 | DAM; 1E6 Hz; ASTM D 150 | |
| Dielectric Constant | 3.4 | 3.4 | DAM; 1E3 Hz; ASTM D 150 | |
| Dielectric Constant | 3.4 | 3.4 | DAM; 1E2 Hz; ASTM D 150 | |
| Dielectric Constant | 3.6 | 3.6 | 50%RH; 1E6 Hz; ASTM D 150 | |
| Dielectric Constant | 5.6 | 5.6 | 50%RH; 1E3 Hz; ASTM D 150 | |
| Dielectric Constant | 7 | 7 | 50%RH; 1E2 Hz; ASTM D 150 | |
| Dissipation Factor | 0.01 | 0.01 | DAM; 1E2 Hz; ASTM D 150 | |
| Dissipation Factor | 0.01 | 0.01 | DAM; 1E3 Hz; ASTM D 150 | |
| Dissipation Factor | 0.02 | 0.02 | DAM; 1E6 Hz; ASTM D 150 | |
| Dissipation Factor | 0.06 | 0.06 | 50%RH; 1E6 Hz; ASTM D 150 | |
| Dissipation Factor | 0.15 | 0.15 | 50%RH; 1E3 Hz; ASTM D 150 | |
| Dissipation Factor | 0.2 | 0.2 | 50%RH; 1E2 Hz; ASTM D 150 | |
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | |
| Comparative Tracking Index | 600 V | 600 V | DAM; UL 746A | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 100 ?m/m-?C | 55.6 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C | 100 ?m/m-?C | 55.6 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 110 ?m/m-?C | 61.1 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 110 ?m/m-?C | 61.1 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| Melting Point | 262 ?C | 504 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Melting Point | 263 ?C | 505 ?F | DAM; ASTM D 3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 ?C | 392 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 ?C | 410 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65 ?C | 149 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70 ?C | 158 ?F | DAM; ISO 75-1/-2 | |
| UL RTI, Electrical | 140 ?C | 284 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Electrical | 140 ?C | 284 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Electrical | 140 ?C | 284 ?F | 0.71mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 110 ?C | 230 ?F | 1.5mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 110 ?C | 230 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical with Impact | 95 ?C | 203 ?F | 0.71mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 115 ?C | 239 ?F | 0.71mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 125 ?C | 257 ?F | 3.0mm; DAM; UL 746B | |
| UL RTI, Mechanical without Impact | 125 ?C | 257 ?F | 1.5mm; DAM; UL 746B | |
| Flammability, UL94 | V-2 | V-2 | 3.0mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | V-2 | V-2 | 3.0mm; DAM; UL94 | |
| Flammability, UL94 | V-2 | V-2 | 1.5mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | V-2 | V-2 | 1.5mm; DAM; UL94 | |
| Flammability, UL94 | V-2 | V-2 | 0.71mm; DAM; IEC 60695-11-10 | |
| Flammability, UL94 | V-2 | V-2 | 0.71mm; DAM; UL94 | |
| Oxygen Index | 28 % | 28 % | DAM; ISO 4589-1/-2 | |
| Glow Wire Test | 725 ?C | 1340 ?F | 0.71mm; DAM; Ignition Temperature; IEC 60695-2-13 | |
| Glow Wire Test | 725 ?C | 1340 ?F | 1.5mm; DAM; Ignition Temperature; IEC 60695-2-13 | |
| Glow Wire Test | 725 ?C | 1340 ?F | 3.0mm; DAM; Ignition Temperature; IEC 60695-2-13 | |
| Glow Wire Test | 850 ?C | 1560 ?F | 0.71mm; DAM; Flammability Index; IEC 60695-2-12 | |
| Glow Wire Test | 960 ?C | 1760 ?F | 3.0mm; DAM; Flammability Index; IEC 60695-2-12 | |
| Glow Wire Test | 960 ?C | 1760 ?F | 1.5mm; DAM; Flammability Index; IEC 60695-2-12 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 280 - 300 ?C | 536 - 572 ?F | ||
| Melt Temperature | 290 ?C | 554 ?F | Optimum | |
| Mold Temperature | 50 - 90 ?C | 122 - 194 ?F | ||
| Mold Temperature | 70 ?C | 158 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Lubricant | |||
| Additive | Mold Release | |||
| Additive | Heat Stabilizer | |||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Unreinforced Resins | |||
| Features | Lubricated | |||
| Features | Cycle (Production), Fast | |||
| Features | Heat Aging Resistance, Good | |||
| Form | Pellets | |||
| Heat Stabilized | Yes | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >PA66< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | PA66 | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Fasteners | |||
| Uses | Electrical/Electronic Applications | |||
| Uses | Automotive Applications | |||
| Uses | Connectors | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.