DuPont Zytel? 114HSL BK000 Nylon 66
Subcategory: Nylon; Nylon 66; Polymer; Thermoplastic
Material Notes:
Zytel? 114HSL BK000 is a heat stabilized, lubricated, modified polyamide 66 resin for injection molding.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.12 g/cc | 0.0405 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.12 g/cc | 0.0405 lb/in? | DAM; ASTM D 792 | |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | 2.0mm; ISO 294-4 | |
Mechanical Properties |
||||
|
||||
| Tensile Strength, Ultimate | 72.3 MPa | 10500 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 70 MPa | 10200 psi | DAM; ISO 527 | |
| Elongation at Break | 20 % | 20 % | DAM; Nominal; ISO 527 | |
| Elongation at Break | 30 % | 30 % | DAM; ASTM D 638 | |
| Elongation at Break | 30 % | 30 % | ISO 527 | |
| Elongation at Yield | 5 % | 5 % | ISO 527 | |
| Tensile Modulus | 2.8 GPa | 406 ksi | DAM; ISO 527 | |
| Flexural Modulus | 2.55 GPa | 370 ksi | DAM; ASTM D 790 | |
| Flexural Modulus | 2.6 GPa | 377 ksi | DAM; ISO 178 | |
| Izod Impact, Notched (ISO) | 11 kJ/m? | 5.23 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | DAM; ISO 180/1U | |
| Izod Impact, Notched, Low Temp (ISO) | 10 kJ/m? | 4.76 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 0.7 J/cm? | 3.33 ft-lb/in? | -40?C; DAM; ISO 179/1eA | |
| Charpy Impact, Notched | 1.5 J/cm? | 7.14 ft-lb/in? | DAM; ISO 179/1eA | |
| Izod Impact, Notched | 0.96 J/cm | 1.8 ft-lb/in | DAM; ASTM D 256 | |
Thermal Properties |
||||
|
||||
| Melting Point | 263 ?C | 505 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Melting Point | 263 ?C | 505 ?F | DAM; ASTM D 3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 ?C | 383 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 ?C | 392 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60 ?C | 140 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65 ?C | 149 ?F | DAM; ISO 75-1/-2 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 280 - 300 ?C | 536 - 572 ?F | ||
| Melt Temperature | 290 ?C | 554 ?F | Optimum | |
| Mold Temperature | 50 - 90 ?C | 122 - 194 ?F | ||
| Mold Temperature | 70 ?C | 158 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | ||
Descriptive Properties |
||||
|
||||
| Additive | Heat Stabilizer | |||
| Additive | Impact Modifier | |||
| Appearance | Black | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Unreinforced Resins | |||
| Features | Cycle (Production), Fast | |||
| Features | Lubricated | |||
| Features | Toughness, Good | |||
| Form | Pellets | |||
| Part Marking Code | >PA66-I< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Resin Identification | PA66-I | ISO 1043 | ||
| Uses | Appliances | |||
| Uses | Automotive Applications | |||
| Uses | Fasteners | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.