DuPont Zytel? 7301 NC010 Nylon 6
Subcategory: Nylon; Nylon 6; Polymer; Thermoplastic
Material Notes:
Zytel? 7301 NC010 is a general purpose, unlubricated polyamide 6 resin for extrusion applications.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.13 g/cc | 0.0408 lb/in? | DAM; ISO 1183 | |
| Specific Gravity | 1.13 g/cc | 0.0408 lb/in? | DAM; ASTM D 792 | |
| Moisture Absorption at Equilibrium | 3 % | 3 % | 50%RH; 23?C; DAM; ISO 62, Similar to | |
| Water Absorption at Saturation | 9.5 % | 9.5 % | Immersed; 23?C; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage | 0.01 cm/cm | 0.01 in/in | Flow 3.0mm (0.118in) | |
Mechanical Properties |
||||
|
||||
| Tensile Strength, Ultimate | 60 MPa | 8700 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Ultimate | 80 MPa | 11600 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 41 MPa | 5950 psi | 50%RH; ASTM D 638 | |
| Tensile Strength, Yield | 50 MPa | 7250 psi | 50%RH; ISO 527 | |
| Tensile Strength, Yield | 80 MPa | 11600 psi | DAM; ASTM D 638 | |
| Tensile Strength, Yield | 80 MPa | 11600 psi | DAM; ISO 527 | |
| Elongation at Break | Min 100 % | Min 100 % | ISO 527 | |
| Elongation at Break | 240 % | 240 % | 50%RH; ASTM D 638 | |
| Elongation at Break | 25 % | 25 % | DAM; Nominal; ISO 527 | |
| Elongation at Break | 50 % | 50 % | ISO 527 | |
| Elongation at Break | 60 % | 60 % | DAM; ASTM D 638 | |
| Elongation at Yield | 23 % | 23 % | ASTM D 638 | |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527 | |
| Elongation at Yield | 4.8 % | 4.8 % | ASTM D 638 | |
| Tensile Modulus | 1.5 GPa | 218 ksi | 50%RH; ISO 527 | |
| Tensile Modulus | 2.9 GPa | 421 ksi | DAM; ISO 527 | |
| Flexural Modulus | 0.695 GPa | 101 ksi | 50%RH; ASTM D 790 | |
| Flexural Modulus | 2.3 GPa | 334 ksi | DAM; ISO 178 | |
| Flexural Modulus | 2.78 GPa | 403 ksi | DAM; ASTM D 790 | |
| Flexural Strength | 110 MPa | 16000 psi | @ 5% Strain; 23?C; DAM; ASTM D 790 | |
| Flexural Strength | 27 MPa | 3920 psi | @ 5% Strain; 23?C; 50%RH; ASTM D 790 | |
| Izod Impact, Notched (ISO) | 6 kJ/m? | 2.86 ft-lb/in? | DAM; ISO 180/1A | |
| Izod Impact, Unnotched | NB | NB | 50%RH; ASTM D 4812 | |
| Izod Impact, Unnotched | NB | NB | DAM; ASTM D 4812 | |
| Izod Impact, Unnotched (ISO) | NB | NB | 50%RH; ISO 180/1U | |
| Izod Impact, Notched, Low Temp (ISO) | 6 kJ/m? | 2.86 ft-lb/in? | -40?C; DAM; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | 50%RH; ISO 179/1eU | |
| Charpy Impact Unnotched | NB | NB | DAM; ISO 179/1eU | |
| Charpy Impact, Unnotched Low Temp | NB | NB | -40?C; DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.6 J/cm? | 2.86 ft-lb/in? | DAM; ISO 179/1eA | |
| Izod Impact, Notched | 0.62 J/cm | 1.16 ft-lb/in | DAM; ASTM D 256 | |
| Izod Impact, Notched | 7.5 J/cm | 14.1 ft-lb/in | 50%RH; ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | 1e+010 ohm-cm | 1e+010 ohm-cm | 50%RH; IEC 60093 | |
| Volume Resistivity | 1e+013 ohm-cm | 1e+013 ohm-cm | DAM; IEC 60093 | |
| Surface Resistance | 1e+010 ohm | 1e+010 ohm | 50%RH; IEC 60167 | |
| Surface Resistance | 1e+013 ohm | 1e+013 ohm | DAM; IEC 60167 | |
| Dielectric Constant | 3.5 | 3.5 | 1E6 Hz; 23?C; DAM; IEC 60250 | |
| Dielectric Constant | 7 | 7 | 1E6 Hz; 23?C; 50%RH; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | 50%RH; IEC 60112 | |
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 70 ?m/m-?C | 38.9 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 70 ?m/m-?C | 38.9 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 100 ?m/m-?C | 55.6 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 100 ?m/m-?C | 55.6 ?in/in-?F | DAM; 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| Melting Point | 220 ?C | 428 ?F | DAM; ASTM D 3418 | |
| Melting Point | 221 ?C | 430 ?F | 10?C/min; DAM; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 ?C | 316 ?F | DAM; ASTM D 648 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 ?C | 320 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55 ?C | 131 ?F | DAM; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55 ?C | 131 ?F | DAM; ASTM D 648 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 230 - 240 ?C | 446 - 464 ?F | Extrusion | |
| Melt Temperature | 260 - 280 ?C | 500 - 536 ?F | Injection Molding | |
| Melt Temperature | 230 ?C | 446 ?F | Optimum; Extrusion | |
| Melt Temperature | 270 ?C | 518 ?F | Optimum; Injection Molding | |
| Mold Temperature | 50 - 90 ?C | 122 - 194 ?F | Injection Molding | |
| Mold Temperature | 70 ?C | 158 ?F | Optimum; Injection Molding | |
| Drying Temperature | 80 ?C | 176 ?F | Injection Molding | |
| Drying Temperature | 80 ?C | 176 ?F | Extrusion | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Injection Molding; Dehumidified Dryer | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | Extrusion; Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | Injection Molding | |
| Moisture Content | Max 0.04 % | Max 0.04 % | Extrusion | |
Descriptive Properties |
||||
|
||||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Extrusion Resins | |||
| DuPont Product Category | Unreinforced Resins | |||
| Features | Chemical Resistance, Good | |||
| Features | Oil Resistant | |||
| Features | Fuel Resistant | |||
| Features | Grease Resistant | |||
| Form | Pellets | |||
| Part Marking Code | >PA6< | ISO 11469 | ||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Resin Identification | PA6 | ISO 1043 | ||
| Uses | Industrial Applications | |||
| Uses | Appliance Components | |||
| Uses | Automotive Applications | |||
| Uses | Electrical/Electronic Applications | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.