SABIC Innovative Plastics LEXAN PC EXL9335 Polycarbonate (Europe)
Subcategory: Polycarbonate; Polymer; Thermoplastic
Close Analogs: Saudi Basic Industries Corporation (SABIC) announced on August 31st, 2007, the completion of its purchase of GE Plastics.
Material Notes:
Information provided by GE Plastics for their European product line. This product is also a part of their North American product line.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.19 g/cc | 0.043 lb/in? | ISO 1183 | |
| Linear Mold Shrinkage | 0.005 - 0.007 cm/cm | 0.005 - 0.007 in/in | Flow; ASTM D 955 | |
| Melt Flow | 10 g/10 min | 10 g/10 min | cm3/10min; Melt Volume Rate, MVR at 300C/1.2 kg; ISO 1133 | |
Mechanical Properties |
||||
|
||||
| Hardness, H358/30 | 90 MPa | 13100 psi | ISO 2039/1 | |
| Tensile Strength, Ultimate | 60 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 125 % | 125 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6 % | 6 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.1 GPa | 305 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 2.2 GPa | 319 ksi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 85 MPa | 12300 psi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.95 J/cm | 14.9 ft-lb/in | 23 C; ASTM D 256 | |
| Izod Impact, Notched (ISO) | 65 kJ/m? | 30.9 ft-lb/in? | 80*10*4 +23 C; ISO 180/ 1A | |
| Izod Impact, Notched (ISO) | 80 kJ/m? | 38.1 ft-lb/in? | 23C, 3.2 mm; ISO 180/ 4A | |
| Izod Impact, Notched, Low Temp (ISO) | 58 kJ/m? | 27.6 ft-lb/in? | 80*10*4 -30 C; ISO 180/ 1A | |
| Izod Impact, Notched, Low Temp | 6.8 J/cm | 12.7 ft-lb/in | at -30 C; ASTM D 256 | |
| Izod Impact, Notched, Low Temp (ISO) | 65 kJ/m? | 30.9 ft-lb/in? | at -30C, 3.2 mm; ISO 180/ 4A | |
| Charpy Impact, Notched, Low Temp | 6 J/cm? | 28.6 ft-lb/in? | at -30C, V-notch Edgew 80*10*4 sp=62; ISO 179/1eA | |
| Charpy Impact, Notched | 7.5 J/cm? | 35.7 ft-lb/in? | 23C, V-notch Edgew 80*10*4 sp=62; ISO 179/1eA | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | Min 1e+015 ohm-cm | Min 1e+015 ohm-cm | IEC 60093 | |
| Surface Resistivity per Square | Min 1e+015 ohm | Min 1e+015 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 2.6 | 2.6 | 50 Hz; IEC 60250 | |
| Dielectric Constant | 2.7 | 2.7 | 1 MHz; IEC 60250 | |
| Dielectric Strength | 16 kV/mm | 406 kV/in | in oil, 3.2 mm; IEC 60243-1 | |
| Dissipation Factor | 0.001 | 0.001 | 50 Hz; IEC 60250 | |
| Dissipation Factor | 0.0085 | 0.0085 | 1 MHz; IEC 60250 | |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112/3rd | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 72 ?m/m-?C | 40 ?in/in-?F | 23C-80C, flow; ISO 11359-2 | |
| CTE, linear 20?C Transverse to Flow | 77 ?m/m-?C | 42.8 ?in/in-?F | 23C-80C; ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 ?C | 275 ?F | HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm; ISO 75/Be | |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 ?C | 255 ?F | HDT/Ae, 1.82 MPa Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| Vicat Softening Point | 140 ?C | 284 ?F | B/50; ISO 306 | |
| Vicat Softening Point | 142 ?C | 288 ?F | B/120; ISO 306 | |
| Flammability, UL94 | V-0 | V-0 | 1.5 mm | |
| Oxygen Index | 35 % | 35 % | ISO 4589 | |
| Glow Wire Test | 960 ?C | 1760 ?F | Passes at 1 mm; IEC 60695-2-1 | |
Descriptive Properties |
||||
|
||||
| Ball Pressure Test, 125 C +/- 2 C | PASS | IEC 60035-1 | ||
|
||||
 Printer friendly version |
||||