DuPont Rynite? PET 415HP NC010 PET

Return to last search
Printer friendly version	Add to Folder:
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program

Subcategory: Polyester, TP; Polyethylene Terephthalate (PET); Polymer; Thermoplastic

Material Notes:
Rynite? 415HP NC010 is a 15% glass reinforced modified polyethylene terephthalate improved for easy, fast processing over a broad molding range with excellent balance of strength, stiffness, and temperature resistance.

No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.

Physical Properties	Metric	English	Comments
Density	1.39 g/cc	0.0502 lb/in?	ISO 1183
Specific Gravity	1.39 g/cc	0.0502 lb/in?	ASTM D 792
Filler Content	15 %	15 %	Glass fiber reinforcement
Water Absorption	0.24 %	0.24 %	50%RH,23?C,24h; 23?C; ASTM D 570
Moisture Absorption at Equilibrium	0.25 %	0.25 %	50%RH; 23?C; ISO 62, Similar to
Water Absorption at Saturation	2.5 %	2.5 %	Immersed; 23?C; ISO 62, Similar to
Linear Mold Shrinkage	0.0024 cm/cm	0.0024 in/in	Flow 1.57mm (0.062in)
Linear Mold Shrinkage	0.0035 cm/cm	0.0035 in/in	Parallel 2.0mm; ISO 294-4
Linear Mold Shrinkage	0.004 cm/cm	0.004 in/in	Flow 3.2mm (0.125in)
Linear Mold Shrinkage	0.0045 cm/cm	0.0045 in/in	Parallel Annealed; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0067 cm/cm	0.0067 in/in	1.57mm (0.062in)
Linear Mold Shrinkage, Transverse	0.0085 cm/cm	0.0085 in/in	2.0mm; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0095 cm/cm	0.0095 in/in	3.2mm (0.125in)
Linear Mold Shrinkage, Transverse	0.012 cm/cm	0.012 in/in	Annealed; ISO 294-4
Mechanical Properties
Hardness, Rockwell M	55	55	ASTM D 785
Hardness, Rockwell M	58	58	ISO 2039/2
Hardness, Rockwell R	110	110	ASTM D 785
Hardness, Rockwell R	111	111	ISO 2039/2
Tensile Strength, Ultimate	145 MPa	21000 psi	-40?C; ASTM D 638
Tensile Strength, Ultimate	35.9 MPa	5210 psi	150?C; ASTM D 638
Tensile Strength, Ultimate	44.8 MPa	6500 psi	90?C; ASTM D 638
Tensile Strength, Ultimate	79 MPa	11500 psi	ASTM D 638
Tensile Strength at Break	79 MPa	11500 psi	ISO 527
Elongation at Break	13 %	13 %	90?C; ASTM D 638
Elongation at Break	14 %	14 %	150?C; ASTM D 638
Elongation at Break	3 %	3 %	-40?C; ASTM D 638
Elongation at Break	5 %	5 %	ISO 527
Elongation at Break	6 %	6 %	ASTM D 638
Tensile Modulus	1.69 GPa	245 ksi	150?C; ASTM D 638
Tensile Modulus	1.83 GPa	265 ksi	90?C; ASTM D 638
Tensile Modulus	4.22 GPa	612 ksi	ASTM D 638
Tensile Modulus	4.7 GPa	682 ksi	ISO 527
Tensile Modulus	6.4 GPa	928 ksi	-40?C; ASTM D 638
Flexural Modulus	1.1 GPa	160 ksi	150?C; ASTM D 790
Flexural Modulus	1.1 GPa	160 ksi	150?C; ISO 178
Flexural Modulus	1.28 GPa	186 ksi	90?C; ASTM D 790
Flexural Modulus	1.3 GPa	189 ksi	93?C; ISO 178
Flexural Modulus	3.55 GPa	515 ksi	ISO 178
Flexural Modulus	3.6 GPa	522 ksi	ASTM D 790
Flexural Modulus	5.86 GPa	850 ksi	-40?C; ASTM D 790
Flexural Modulus	5.9 GPa	856 ksi	-40?C; ISO 178
Flexural Strength	210 MPa	30500 psi	-40?C; ASTM D 790
Flexural Strength	34.5 MPa	5000 psi	150?C; ASTM D 790
Flexural Strength	48.3 MPa	7010 psi	90?C; ASTM D 790
Flexural Strength	93.1 MPa	13500 psi	ASTM D 790
Compressive Strength	93 MPa	13500 psi	ASTM D 695
Shear Strength	40 MPa	5800 psi	ASTM D 732
Izod Impact, Notched (ISO)	13 kJ/m?	6.19 ft-lb/in?	ISO 180/1A
Izod Impact, Unnotched	8.55 J/cm	16 ft-lb/in	ASTM D 4812
Izod Impact, Unnotched Low Temp	6.4 J/cm	12 ft-lb/in	-40?C; ASTM D 4812
Izod Impact, Notched, Low Temp (ISO)	7.7 kJ/m?	3.66 ft-lb/in?	-30?C; ISO 180/1A
Charpy Impact Unnotched	5.5 J/cm?	26.2 ft-lb/in?	ISO 179/1eU
Charpy Impact, Notched, Low Temp	0.8 J/cm?	3.81 ft-lb/in?	-30?C; ISO 179/1eA
Charpy Impact, Unnotched Low Temp	2.5 J/cm?	11.9 ft-lb/in?	-30?C; ISO 179/1eU
Charpy Impact, Notched	1.1 J/cm?	5.24 ft-lb/in?	ISO 179/1eA
Izod Impact, Notched	1.33 J/cm	2.49 ft-lb/in	ASTM D 256
Izod Impact, Notched	0.69 J/cm	1.29 ft-lb/in	-40?C; ASTM D 256
Electrical Properties
Volume Resistivity	1e+011 ohm-cm	1e+011 ohm-cm	ASTM D 257
Volume Resistivity	1e+011 ohm-cm	1e+011 ohm-cm	IEC 60093
Surface Resistance	1e+013 ohm	1e+013 ohm	ASTM D 257
Surface Resistance	1e+013 ohm	1e+013 ohm	IEC 60093
Dielectric Constant	3.7	3.7	1E6 Hz; ASTM D 150
Dielectric Constant	3.9	3.9	1E3 Hz; ASTM D 150
Dielectric Strength	11 kV/mm	279 kV/in	95?C; 3.2mm (0.125in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	15.5 kV/mm	394 kV/in	95?C; 1.6mm (0.062in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	18 kV/mm	457 kV/in	23?C; 3.2mm (0.125in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	24 kV/mm	610 kV/in	23?C; 1.6mm (0.062in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	6.5 kV/mm	165 kV/in	150?C; 3.2mm (0.125in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	8.5 kV/mm	216 kV/in	150?C; 1.6mm (0.062in); Short Time; 500 V/s in oil; ASTM D 149
Dissipation Factor	0.019	0.019	1E3 Hz; ASTM D 150
Dissipation Factor	0.022	0.022	1E6 Hz; ASTM D 150
Comparative Tracking Index	275 V	275 V	23?C; 3.0mm; UL 746A
Thermal Properties
CTE, linear 20?C	20 ?m/m-?C	11.1 ?in/in-?F	23 - 55?C (73 - 130?F); Parallel; ASTM E 831
CTE, linear 20?C	20 ?m/m-?C	11.1 ?in/in-?F	23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2
CTE, linear 20?C	23 ?m/m-?C	12.8 ?in/in-?F	2.0mm; 23 - 55?C (73 - 130?F); Parallel; ASTM E 831
CTE, linear 20?C	23 ?m/m-?C	12.8 ?in/in-?F	2.0mm; 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2
CTE, linear 20?C	40 ?m/m-?C	22.2 ?in/in-?F	-40 - 23?C (-40 - 73?F); Parallel; ASTM E 831
CTE, linear 20?C	40 ?m/m-?C	22.2 ?in/in-?F	-40 - 23?C (-40 - 73?F); Parallel; ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	109 ?m/m-?C	60.6 ?in/in-?F	55 - 160?C (130 - 320?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	109 ?m/m-?C	60.6 ?in/in-?F	55 - 160?C (130 - 320?F); ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	117 ?m/m-?C	65 ?in/in-?F	23 - 55?C (73 - 130?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	117 ?m/m-?C	65 ?in/in-?F	23 - 55?C (73 - 130?F); ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	130 ?m/m-?C	72.2 ?in/in-?F	2.0mm; 23 - 55?C (73 - 130?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	130 ?m/m-?C	72.2 ?in/in-?F	2.0mm; 23 - 55?C (73 - 130?F); ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	98 ?m/m-?C	54.4 ?in/in-?F	-40 - 23?C (-40 - 73?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	98 ?m/m-?C	54.4 ?in/in-?F	-40 - 23?C (-40 - 73?F); ISO 11359-1/-2
CTE, linear 100?C	32 ?m/m-?C	17.8 ?in/in-?F	55 - 160?C (130 - 320?F); Parallel; ASTM E 831
CTE, linear 100?C	32 ?m/m-?C	17.8 ?in/in-?F	55 - 160?C (130 - 320?F); Parallel; ISO 11359-1/-2
Melting Point	250 ?C	482 ?F	ASTM D 3418
Melting Point	250 ?C	482 ?F	10?C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	235 ?C	455 ?F	ASTM D 648
Deflection Temperature at 0.46 MPa (66 psi)	238 ?C	460 ?F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	207 ?C	405 ?F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	207 ?C	405 ?F	ASTM D 648
UL RTI, Electrical	140 ?C	284 ?F	3.0mm; UL 746B
UL RTI, Electrical	140 ?C	284 ?F	1.5mm; UL 746B
UL RTI, Electrical	140 ?C	284 ?F	0.75mm; UL 746B
UL RTI, Mechanical with Impact	120 ?C	248 ?F	0.75mm; UL 746B
UL RTI, Mechanical with Impact	120 ?C	248 ?F	1.5mm; UL 746B
UL RTI, Mechanical with Impact	120 ?C	248 ?F	3.0mm; UL 746B
UL RTI, Mechanical without Impact	140 ?C	284 ?F	3.0mm; UL 746B
UL RTI, Mechanical without Impact	140 ?C	284 ?F	1.5mm; UL 746B
UL RTI, Mechanical without Impact	140 ?C	284 ?F	0.75mm; UL 746B
Flammability, UL94	HB	HB	3.0mm; IEC 60695-11-10
Flammability, UL94	HB	HB	3.0mm; UL94
Flammability, UL94	HB	HB	1.5mm; IEC 60695-11-10
Flammability, UL94	HB	HB	1.5mm; UL94
Flammability, UL94	HB	HB	0.75mm; IEC 60695-11-10
Flammability, UL94	HB	HB	0.75mm; UL94
Oxygen Index	19 %	19 %	ASTM D 2863
Oxygen Index	19 %	19 %	ISO 4589-1/-2
Glow Wire Test	675 ?C	1250 ?F	0.75mm; Flammability Index; IEC 60695-2-12
Glow Wire Test	675 ?C	1250 ?F	1.5mm; Flammability Index; IEC 60695-2-12
Glow Wire Test	700 ?C	1290 ?F	0.75mm; Ignition Temperature; IEC 60695-2-13
Glow Wire Test	700 ?C	1290 ?F	1.5mm; Ignition Temperature; IEC 60695-2-13
Glow Wire Test	750 ?C	1380 ?F	3.0mm; Flammability Index; IEC 60695-2-12
Glow Wire Test	775 ?C	1430 ?F	3.0mm; Ignition Temperature; IEC 60695-2-13
Processing Properties
Melt Temperature	270 - 290 ?C	518 - 554 ?F
Melt Temperature	280 ?C	536 ?F	Optimum
Mold Temperature	Min 95 ?C	Min 203 ?F
Mold Temperature	110 ?C	230 ?F	Optimum
Drying Temperature	120 ?C	248 ?F
Dry Time	4 hour	4 hour	Dehumidified Dryer
Moisture Content	Max 0.02 %	Max 0.02 %
Descriptive Properties
Additive	Impact Modifier
Appearance	Natural Color
Drying	Recommended
DuPont Product Category	Toughened Resins
DuPont Product Category	Glass Reinforced Resins
Features	Strength, Good
Features	Flow, Good
Features	Impact Modified
Features	Impact Resistance, Good
Features	Stiffness, Good
Features	Thermal Aging Resistance, Good
Form	Pellets
Heat Stabilized	Yes
Injection Moldable	Yes
Part Marking Code	>PET-IGF15<	ISO 11469
Processing Method	Injection Molding
Region	Americas
Region	Asia/Pacific
Region	Europe
Resin Identification	PET-IGF15	ISO 1043
Ultrasonic Weldable	Yes
Uses	Electrical/Electronic Applications
Uses	Housings
Uses	Parts, Thin-walled
Printer friendly version