DuPont Rynite? PET SST35 NC010 PET

Return to last search
Printer friendly version	Add to Folder:
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program

Subcategory: Polyester, TP; Polyethylene Terephthalate (PET); Polymer; Thermoplastic

Material Notes:
Rynite? SST35 NC010 is a 35% stiffened super tough glass reinforced modified polyethylene terephthalate with superior combination of toughness and stiffness. Excellent surface appearance, moldability, and temperature resistance.

No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.

Physical Properties	Metric	English	Comments
Specific Gravity	1.52 g/cc	0.0549 lb/in?	ASTM D 792
Filler Content	35 %	35 %	Glass fiber reinforcement
Water Absorption	0.25 %	0.25 %	50%RH,23?C,24h; 23?C; ASTM D 570
Linear Mold Shrinkage	0.0013 cm/cm	0.0013 in/in	Flow 1.57mm (0.062in)
Linear Mold Shrinkage	0.0025 cm/cm	0.0025 in/in	Flow 3.2mm (0.125in)
Linear Mold Shrinkage, Transverse	0.0059 cm/cm	0.0059 in/in	1.57mm (0.062in)
Linear Mold Shrinkage, Transverse	0.0085 cm/cm	0.0085 in/in	3.2mm (0.125in)
Mechanical Properties
Hardness, Rockwell M	50	50	ASTM D 785
Hardness, Rockwell R	105	105	ASTM D 785
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D 638
Tensile Strength, Ultimate	190 MPa	27600 psi	-40?C; ASTM D 638
Tensile Strength, Ultimate	44.8 MPa	6500 psi	150?C; ASTM D 638
Tensile Strength, Ultimate	55.2 MPa	8010 psi	90?C; ASTM D 638
Elongation at Break	3.2 %	3.2 %	-40?C; ASTM D 638
Elongation at Break	5 %	5 %	ASTM D 638
Elongation at Break	8.5 %	8.5 %	150?C; ASTM D 638
Elongation at Break	8.5 %	8.5 %	90?C; ASTM D 638
Tensile Modulus	10.9 GPa	1580 ksi	-40?C; ASTM D 638
Tensile Modulus	2.3 GPa	334 ksi	150?C; ASTM D 638
Tensile Modulus	3.24 GPa	470 ksi	90?C; ASTM D 638
Tensile Modulus	7.59 GPa	1100 ksi	ASTM D 638
Flexural Modulus	1.9 GPa	276 ksi	150?C; ASTM D 790
Flexural Modulus	2.48 GPa	360 ksi	90?C; ASTM D 790
Flexural Modulus	6.89 GPa	999 ksi	ASTM D 790
Flexural Modulus	8.97 GPa	1300 ksi	-40?C; ASTM D 790
Flexural Strength	145 MPa	21000 psi	ASTM D 790
Flexural Strength	276 MPa	40000 psi	-40?C; ASTM D 790
Flexural Strength	69 MPa	10000 psi	90?C; ASTM D 790
Compressive Strength	81 MPa	11700 psi	ASTM D 695
Shear Strength	38 MPa	5510 psi	ASTM D 732
Izod Impact, Unnotched	12 J/cm	22.5 ft-lb/in	ASTM D 4812
Izod Impact, Unnotched Low Temp	10.7 J/cm	20 ft-lb/in	-40?C; ASTM D 4812
Izod Impact, Notched	1.6 J/cm	3 ft-lb/in	-40?C; ASTM D 256
Izod Impact, Notched	2.35 J/cm	4.4 ft-lb/in	ASTM D 256
Electrical Properties
Volume Resistivity	1e+014 ohm-cm	1e+014 ohm-cm	ASTM D 257
Surface Resistance	1e+013 ohm	1e+013 ohm	ASTM D 257
Dielectric Constant	4.1	4.1	1E6 Hz; ASTM D 150
Dielectric Strength	10.5 kV/mm	267 kV/in	95?C; 3.2mm (0.125in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	16 kV/mm	406 kV/in	95?C; 1.6mm (0.062in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	19.5 kV/mm	495 kV/in	23?C; 3.2mm (0.125in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	25.5 kV/mm	648 kV/in	23?C; 1.6mm (0.062in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	7.5 kV/mm	191 kV/in	150?C; 3.2mm (0.125in); Short Time; 500 V/s in oil; ASTM D 149
Dielectric Strength	9.5 kV/mm	241 kV/in	150?C; 1.6mm (0.062in); Short Time; 500 V/s in oil; ASTM D 149
Dissipation Factor	0.023	0.023	1E6 Hz; ASTM D 150
Comparative Tracking Index	500 V	500 V	IEC 60112
Comparative Tracking Index	500 V	500 V	23?C; 3.0mm; UL 746A
Thermal Properties
CTE, linear 20?C	21 ?m/m-?C	11.7 ?in/in-?F	-40 - 23?C (-40 - 73?F); Parallel; ASTM E 831
CTE, linear 20?C	21 ?m/m-?C	11.7 ?in/in-?F	-40 - 23?C (-40 - 73?F); Parallel; ISO 11359-1/-2
CTE, linear 20?C	6 ?m/m-?C	3.33 ?in/in-?F	23 - 55?C (73 - 130?F); Parallel; ASTM E 831
CTE, linear 20?C	6 ?m/m-?C	3.33 ?in/in-?F	23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	112 ?m/m-?C	62.2 ?in/in-?F	55 - 160?C (130 - 320?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	112 ?m/m-?C	62.2 ?in/in-?F	55 - 160?C (130 - 320?F); ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	113 ?m/m-?C	62.8 ?in/in-?F	-40 - 23?C (-40 - 73?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	113 ?m/m-?C	62.8 ?in/in-?F	-40 - 23?C (-40 - 73?F); ISO 11359-1/-2
CTE, linear 20?C Transverse to Flow	126 ?m/m-?C	70 ?in/in-?F	23 - 55?C (73 - 130?F); ASTM E 831
CTE, linear 20?C Transverse to Flow	126 ?m/m-?C	70 ?in/in-?F	23 - 55?C (73 - 130?F); ISO 11359-1/-2
CTE, linear 100?C	13 ?m/m-?C	7.22 ?in/in-?F	55 - 160?C (130 - 320?F); Parallel; ASTM E 831
CTE, linear 100?C	13 ?m/m-?C	7.22 ?in/in-?F	55 - 160?C (130 - 320?F); Parallel; ISO 11359-1/-2
Melting Point	250 ?C	482 ?F	ASTM D 3418
Deflection Temperature at 0.46 MPa (66 psi)	246 ?C	475 ?F	ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	220 ?C	428 ?F	ASTM D 648
UL RTI, Electrical	150 ?C	302 ?F	3.0mm; UL 746B
UL RTI, Electrical	150 ?C	302 ?F	1.5mm; UL 746B
UL RTI, Electrical	150 ?C	302 ?F	0.75mm; UL 746B
UL RTI, Mechanical with Impact	150 ?C	302 ?F	0.75mm; UL 746B
UL RTI, Mechanical with Impact	150 ?C	302 ?F	1.5mm; UL 746B
UL RTI, Mechanical with Impact	150 ?C	302 ?F	3.0mm; UL 746B
UL RTI, Mechanical without Impact	150 ?C	302 ?F	3.0mm; UL 746B
UL RTI, Mechanical without Impact	150 ?C	302 ?F	1.5mm; UL 746B
UL RTI, Mechanical without Impact	150 ?C	302 ?F	0.75mm; UL 746B
Flammability, UL94	HB	HB	3.0mm; IEC 60695-11-10
Flammability, UL94	HB	HB	3.0mm; UL94
Flammability, UL94	HB	HB	1.5mm; IEC 60695-11-10
Flammability, UL94	HB	HB	1.5mm; UL94
Flammability, UL94	HB	HB	0.75mm; IEC 60695-11-10
Flammability, UL94	HB	HB	0.75mm; UL94
Glow Wire Test	725 ?C	1340 ?F	1.5mm; Flammability Index; IEC 60695-2-12
Glow Wire Test	750 ?C	1380 ?F	1.5mm; Ignition Temperature; IEC 60695-2-13
Glow Wire Test	775 ?C	1430 ?F	0.75mm; Flammability Index; IEC 60695-2-12
Glow Wire Test	800 ?C	1470 ?F	0.75mm; Ignition Temperature; IEC 60695-2-13
Glow Wire Test	825 ?C	1520 ?F	3.0mm; Ignition Temperature; IEC 60695-2-13
Glow Wire Test	825 ?C	1520 ?F	3.0mm; Flammability Index; IEC 60695-2-12
Processing Properties
Melt Temperature	270 - 290 ?C	518 - 554 ?F
Melt Temperature	280 ?C	536 ?F	Optimum
Mold Temperature	Min 95 ?C	Min 203 ?F
Mold Temperature	110 ?C	230 ?F	Optimum
Drying Temperature	120 ?C	248 ?F
Dry Time	4 hour	4 hour	Dehumidified Dryer
Moisture Content	Max 0.02 %	Max 0.02 %
Descriptive Properties
Additive	Impact Modifier
Appearance	Natural Color
DuPont Product Category	Toughened Resins
DuPont Product Category	Glass Reinforced Resins
Features	Thermal Aging Resistance, Good
Features	Impact Modified
Features	Impact Resistance, Good
Features	Stiffness, Good
Features	Strength, Good
Form	Pellets
Heat Stabilized	Yes
Injection Moldable	Yes
Processing Method	Injection Molding
Region	Americas
Ultrasonic Weldable	Yes
Uses	Automotive Applications
Uses	Housings
Uses	Structural Parts
Printer friendly version

Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.