DuPont Delrin? 100P NC010 Acetal (POM) Homopolymer
Subcategory: Acetal; Polymer; Thermoplastic
Material Notes:
Delrin? 100P is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin? 100P provides maximum toughness in the product line without modification. Delrin? 100P has improved processing thermal stability.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.42 g/cc | 0.0513 lb/in? | ISO 1183 | |
| Specific Gravity | 1.42 g/cc | 0.0513 lb/in? | ASTM D 792 | |
| Water Absorption | 0.4 % | 0.4 % | Immersion 24h; 23?C; ASTM D 570 | |
| Moisture Absorption at Equilibrium | 0.28 % | 0.28 % | 50%RH; 23?C; ASTM D 570 | |
| Moisture Absorption at Equilibrium | 0.3 % | 0.3 % | 50%RH; 23?C; ISO 62, Similar to | |
| Water Absorption at Saturation | 1.4 % | 1.4 % | ASTM D 570 | |
| Water Absorption at Saturation | 1.4 % | 1.4 % | Immersed; 23?C; ISO 62, Similar to | |
| Linear Mold Shrinkage | 0.018 - 0.021 cm/cm | 0.018 - 0.021 in/in | Flow 3.2mm (0.125in); 24 h; ASTM D 955 | |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.017 - 0.019 cm/cm | 0.017 - 0.019 in/in | 3.2mm (0.125in); 24 h; ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.02 cm/cm | 0.02 in/in | 2.0mm; ISO 294-4 | |
| Melt Flow | 1 g/10 min | 1 g/10 min | 1.05kg at 190?C; ASTM D 1238 | |
| Melt Flow | 1.9 g/10 min | 1.9 g/10 min | 2.16 kg/190?C; based on room temperature density; ISO 1133 | |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | 190?C, 2.16kg; ISO 1133 | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell M | 92 | 92 | ISO 2039/2 | |
| Hardness, Rockwell R | 120 | 120 | ASTM D 785 | |
| Hardness, Rockwell R | 120 | 120 | ISO 2039/2 | |
| Tensile Strength, Ultimate | 31 MPa | 4500 psi | 5mm/min (0.2in/min); 100?C; ASTM D 638 | |
| Tensile Strength, Ultimate | 67 MPa | 9720 psi | 5mm/min (0.2in/min); 23?C; ASTM D 638 | |
| Tensile Strength, Ultimate | 95 MPa | 13800 psi | 5mm/min (0.2in/min); -40?C; ASTM D 638 | |
| Tensile Strength, Yield | 26 MPa | 3770 psi | 5mm/min (0.2in/min); 100?C; ASTM D 638 | |
| Tensile Strength, Yield | 67 MPa | 9720 psi | 5mm/min (0.2in/min); 23?C; ASTM D 638 | |
| Tensile Strength, Yield | 70 MPa | 10200 psi | ISO 527 | |
| Tensile Strength, Yield | 93 MPa | 13500 psi | 5mm/min (0.2in/min); -40?C; ASTM D 638 | |
| Elongation at Break | Min 250 % | Min 250 % | 5mm/min (0.2in/min); 100?C; ASTM D 638 | |
| Elongation at Break | 40 % | 40 % | 5mm/min (0.2in/min); -40?C; ASTM D 638 | |
| Elongation at Break | 45 % | 45 % | Nominal; ISO 527 | |
| Elongation at Break | 65 % | 65 % | ISO 527 | |
| Elongation at Break | 80 % | 80 % | 5mm/min (0.2in/min); 23?C; ASTM D 638 | |
| Elongation at Yield | 10 % | 10 % | ASTM D 638 | |
| Elongation at Yield | 21 % | 21 % | ASTM D 638 | |
| Elongation at Yield | 23 % | 23 % | ASTM D 638 | |
| Elongation at Yield | 25 % | 25 % | ISO 527 | |
| Tensile Modulus | 0.76 GPa | 110 ksi | 5mm/min (0.2in/min); 100?C; ASTM D 638 | |
| Tensile Modulus | 2.9 GPa | 421 ksi | ISO 527 | |
| Tensile Modulus | 2.94 GPa | 426 ksi | 5mm/min (0.2in/min); 23?C; ASTM D 638 | |
| Tensile Modulus | 3.31 GPa | 480 ksi | 5mm/min (0.2in/min); -40?C; ASTM D 638 | |
| Flexural Modulus | 0.76 GPa | 110 ksi | 100?C; ASTM D 790 | |
| Flexural Modulus | 2.6 GPa | 377 ksi | ISO 178 | |
| Flexural Modulus | 2.79 GPa | 405 ksi | ASTM D 790 | |
| Flexural Modulus | 3.13 GPa | 454 ksi | -40?C; ASTM D 790 | |
| Flexural Yield Strength | 74 MPa | 10700 psi | @ 3.5% Strain; 23?C; Flexural Stress; ISO 178 | |
| Flexural Yield Strength | 94 MPa | 13600 psi | @ 5% Strain; 23?C; Flexural Stress; ASTM D 790 | |
| Shear Strength | 62 MPa | 8990 psi | ASTM D 732 | |
| Izod Impact, Notched (ISO) | 14 kJ/m? | 6.66 ft-lb/in? | ISO 180/1A | |
| Izod Impact, Unnotched | NB | NB | ASTM D 4812 | |
| Izod Impact, Notched, Low Temp (ISO) | 12 kJ/m? | 5.71 ft-lb/in? | -40?C; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 1.1 J/cm? | 5.24 ft-lb/in? | -30?C; ISO 179/1eA | |
| Charpy Impact, Unnotched Low Temp | 35 J/cm? | 167 ft-lb/in? | -30?C; ISO 179/1eU | |
| Charpy Impact, Notched | 1.4 J/cm? | 6.66 ft-lb/in? | ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 2700 MPa | 392000 psi | ISO 899 | |
| Tensile Creep Modulus, 1000 hours | 1500 MPa | 218000 psi | ISO 899 | |
| Izod Impact, Notched | 1.2 J/cm | 2.25 ft-lb/in | ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | 1e+012 ohm-cm | 1e+012 ohm-cm | IEC 60093 | |
| Volume Resistivity | 4e+014 ohm-cm | 4e+014 ohm-cm | ASTM D 257 | |
| Surface Resistance | Min 1e+015 ohm | Min 1e+015 ohm | IEC 60093 | |
| Surface Resistance | 2e+014 ohm | 2e+014 ohm | ASTM D 257 | |
| Dielectric Constant | 3.7 | 3.7 | 1E6 Hz; ASTM D 150 | |
| Dielectric Constant | 3.7 | 3.7 | 1E6 Hz; 23?C; IEC 60250 | |
| Dielectric Constant | 3.8 | 3.8 | 1E2 Hz; 23?C; IEC 60250 | |
| Dielectric Strength | 16.9 kV/mm | 429 kV/in | 23?C; 3.2mm (0.125in); Short Time; ASTM D 149 | |
| Dielectric Strength | 32 kV/mm | 813 kV/in | 1.0mm; IEC 60243-1 | |
| Dissipation Factor | 0.004 | 0.004 | 1E6 Hz; IEC 60250 | |
| Dissipation Factor | 0.005 | 0.005 | 1E6 Hz; ASTM D 150 | |
| Dissipation Factor | 0.02 | 0.02 | 1E2 Hz; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | |
| Comparative Tracking Index | 600 V | 600 V | 23?C; 3.0mm; UL 746A | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 105 ?m/m-?C | 58.3 ?in/in-?F | -40 - 23?C (-40 - 73?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 110 ?m/m-?C | 61.1 ?in/in-?F | 23 - 55?C (73 - 130?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 110 ?m/m-?C | 61.1 ?in/in-?F | -40 - 23?C (-40 - 73?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C | 110 ?m/m-?C | 61.1 ?in/in-?F | 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 100 ?m/m-?C | 55.6 ?in/in-?F | -40 - 23?C (-40 - 73?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 100 ?m/m-?C | 55.6 ?in/in-?F | -40 - 23?C (-40 - 73?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 110 ?m/m-?C | 61.1 ?in/in-?F | 23 - 55?C (73 - 130?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 110 ?m/m-?C | 61.1 ?in/in-?F | 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 148 ?m/m-?C | 82.2 ?in/in-?F | 55 - 100?C (130 - 212?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 150 ?m/m-?C | 83.3 ?in/in-?F | 55 - 100?C (130 - 212?F); ISO 11359-1/-2 | |
| CTE, linear 100?C | 150 ?m/m-?C | 83.3 ?in/in-?F | 55 - 100?C (130 - 212?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 100?C | 151 ?m/m-?C | 83.9 ?in/in-?F | 55 - 100?C (130 - 212?F); Parallel; ASTM E 831 | |
| Melting Point | 178 ?C | 352 ?F | ASTM D 3418 | |
| Melting Point | 178 ?C | 352 ?F | 10?C/min; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 ?C | 320 ?F | ISO 75-1/-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 ?C | 325 ?F | Not Annealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 ?C | 230 ?F | Annealed; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93 ?C | 199 ?F | ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95 ?C | 203 ?F | Not Annealed; ASTM D 648 | |
| UL RTI, Electrical | 110 ?C | 230 ?F | 3.0mm; UL 746B | |
| UL RTI, Electrical | 110 ?C | 230 ?F | 1.5mm; UL 746B | |
| UL RTI, Electrical | 50 ?C | 122 ?F | 0.75mm; UL 746B | |
| UL RTI, Mechanical with Impact | 50 ?C | 122 ?F | 0.75mm; UL 746B | |
| UL RTI, Mechanical with Impact | 85 ?C | 185 ?F | 1.5mm; UL 746B | |
| UL RTI, Mechanical with Impact | 90 ?C | 194 ?F | 3.0mm; UL 746B | |
| UL RTI, Mechanical without Impact | 50 ?C | 122 ?F | 0.75mm; UL 746B | |
| UL RTI, Mechanical without Impact | 90 ?C | 194 ?F | 1.5mm; UL 746B | |
| UL RTI, Mechanical without Impact | 95 ?C | 203 ?F | 3.0mm; UL 746B | |
| Flammability, UL94 | HB | HB | 3.0mm; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 1.5mm; UL94 | |
| Flammability, UL94 | HB | HB | 0.75mm; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 0.75mm; UL94 | |
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 210 - 220 ?C | 410 - 428 ?F | ||
| Melt Temperature | 215 ?C | 419 ?F | Optimum | |
| Mold Temperature | 80 - 100 ?C | 176 - 212 ?F | ||
| Mold Temperature | 90 ?C | 194 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.2 % | Max 0.2 % | ||
Descriptive Properties |
||||
|
||||
| Appearance | Natural Color | |||
| Drying | Not normally required | Unless moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Unreinforced Resins | |||
| Extrudable | Cast Film | |||
| Extrudable | Sheet | |||
| Extrudable | Tubing | |||
| Extrudable | Wire and Cable | |||
| Features | Dimensional Stability, Good | |||
| Features | Toughness, Good | |||
| Features | Viscosity, High | |||
| Form | Pellets | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >POM< | ISO 11469 | ||
| Processing Method | Extrusion | |||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | POM | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Conveyors | |||
| Uses | Fasteners | |||
| Uses | Gears | |||
| Uses | Parts, Engineering | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.