DuPont Delrin? 100ST NC010 Acetal (POM) Homopolymer
Subcategory: Acetal; Polymer; Thermoplastic
Material Notes:
Delrin? 100ST NC010 is a super tough, high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed parts where outstanding toughness is essential.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.34 g/cc | 0.0484 lb/in? | ISO 1183 | |
| Specific Gravity | 1.34 g/cc | 0.0484 lb/in? | ASTM D 792 | |
| Water Absorption | 0.44 % | 0.44 % | Immersion 24h; 23?C; ASTM D 570 | |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 50%RH; 23?C; ASTM D 570 | |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 50%RH; 23?C; ISO 62, Similar to | |
| Water Absorption at Saturation | 0.85 % | 0.85 % | ASTM D 570 | |
| Water Absorption at Saturation | 0.9 % | 0.9 % | Immersed; 23?C; ISO 62, Similar to | |
| Linear Mold Shrinkage | 0.009 - 0.012 cm/cm | 0.009 - 0.012 in/in | Flow 3.2mm (0.125in); 24 h; ASTM D 955 | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Parallel 2.0mm; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.01 - 0.013 cm/cm | 0.01 - 0.013 in/in | 3.2mm (0.125in); 24 h; ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 2.0mm; ISO 294-4 | |
| Melt Flow | 0.8 g/10 min | 0.8 g/10 min | 1.05kg at 190?C; ASTM D 1238 | |
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | 2.16 kg/190?C; based on room temperature density; ISO 1133 | |
| Melt Flow | 2 g/10 min | 2 g/10 min | 190?C, 2.16kg; ISO 1133 | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell M | 58 | 58 | ASTM D 785 | |
| Hardness, Rockwell M | 58 | 58 | ISO 2039/2 | |
| Hardness, Rockwell R | 105 | 105 | ASTM D 785 | |
| Hardness, Rockwell R | 105 | 105 | ISO 2039/2 | |
| Tensile Strength, Ultimate | 18 MPa | 2610 psi | 50mm/min (2.0in/min); 121?C; ASTM D 638 | |
| Tensile Strength, Ultimate | 23 MPa | 3340 psi | 50mm/min (2.0in/min); 100?C; ASTM D 638 | |
| Tensile Strength, Ultimate | 32 MPa | 4640 psi | 50mm/min (2.0in/min); 70?C; ASTM D 638 | |
| Tensile Strength, Yield | 41 MPa | 5950 psi | ISO 527 | |
| Tensile Strength, Yield | 45 MPa | 6530 psi | 50mm/min (2.0in/min); 23?C; ASTM D 638 | |
| Elongation at Break | Min 50 % | Min 50 % | Nominal; ISO 527 | |
| Elongation at Break | Min 100 % | Min 100 % | ISO 527 | |
| Elongation at Break | Min 150 % | Min 150 % | 50mm/min (2.0in/min); 23?C; ASTM D 638 | |
| Elongation at Break | Min 250 % | Min 250 % | 50mm/min (2.0in/min); 100?C; ASTM D 638 | |
| Elongation at Break | Min 250 % | Min 250 % | 50mm/min (2.0in/min); 70?C; ASTM D 638 | |
| Elongation at Yield | 30 % | 30 % | ISO 527 | |
| Elongation at Yield | 35 % | 35 % | ASTM D 638 | |
| Tensile Modulus | 1.3 GPa | 189 ksi | 50mm/min (2.0in/min); 23?C; ASTM D 638 | |
| Tensile Modulus | 1.4 GPa | 203 ksi | ISO 527 | |
| Flexural Modulus | 0.2 GPa | 29 ksi | 121?C; ASTM D 790 | |
| Flexural Modulus | 0.35 GPa | 50.8 ksi | 100?C; ASTM D 790 | |
| Flexural Modulus | 0.7 GPa | 102 ksi | 70?C; ASTM D 790 | |
| Flexural Modulus | 1.1 GPa | 160 ksi | ISO 178 | |
| Flexural Modulus | 1.13 GPa | 164 ksi | ASTM D 790 | |
| Flexural Yield Strength | 34 MPa | 4930 psi | @ 3.5% Strain; 23?C; Flexural Stress; ISO 178 | |
| Flexural Yield Strength | 36 MPa | 5220 psi | @ 5% Strain; 23?C; Flexural Stress; ASTM D 790 | |
| Shear Strength | 34 MPa | 4930 psi | ASTM D 732 | |
| Izod Impact, Notched (ISO) | 90 kJ/m? | 42.8 ft-lb/in? | ISO 180/1A | |
| Izod Impact, Unnotched | NB | NB | ASTM D 4812 | |
| Izod Impact, Notched, Low Temp (ISO) | 20 kJ/m? | 9.52 ft-lb/in? | -40?C; ISO 180/1A | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | |
| Charpy Impact, Notched, Low Temp | 2 J/cm? | 9.52 ft-lb/in? | -30?C; ISO 179/1eA | |
| Charpy Impact, Unnotched Low Temp | NB | NB | -30?C; ISO 179/1eU | |
| Charpy Impact, Notched | 9 J/cm? | 42.8 ft-lb/in? | ISO 179/1eA | |
| Tensile Impact Strength | 1580 kJ/m? | 752 ft-lb/in? | 23?C; Long specimen; ASTM D 1822 | |
| Tensile Creep Modulus, 1 hour | 1350 MPa | 196000 psi | ISO 899 | |
| Tensile Creep Modulus, 1000 hours | 550 MPa | 79800 psi | ISO 899 | |
| Izod Impact, Notched | 2.5 J/cm | 4.68 ft-lb/in | -40?C; ASTM D 256 | |
| Izod Impact, Notched | NB | NB | ASTM D 256 | |
Electrical Properties |
||||
|
||||
| Volume Resistivity | 1e+012 ohm-cm | 1e+012 ohm-cm | IEC 60093 | |
| Volume Resistivity | 4e+014 ohm-cm | 4e+014 ohm-cm | ASTM D 257 | |
| Surface Resistance | 1e+014 ohm | 1e+014 ohm | IEC 60093 | |
| Surface Resistance | 2e+014 ohm | 2e+014 ohm | ASTM D 257 | |
| Dielectric Constant | 3.8 | 3.8 | 1E6 Hz; 23?C; IEC 60250 | |
| Dielectric Constant | 4.2 | 4.2 | 1E6 Hz; ASTM D 150 | |
| Dielectric Constant | 4.4 | 4.4 | 1E2 Hz; 23?C; IEC 60250 | |
| Dielectric Strength | 20 kV/mm | 508 kV/in | 23?C; 3.2mm (0.125in); Short Time; ASTM D 149 | |
| Dielectric Strength | 39 kV/mm | 991 kV/in | 1.0mm; IEC 60243-1 | |
| Dissipation Factor | 0.0065 | 0.0065 | 1E2 Hz; IEC 60250 | |
| Dissipation Factor | 0.027 | 0.027 | 1E6 Hz; ASTM D 150 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | |
| Comparative Tracking Index | 600 V | 600 V | 23?C; 3.0mm; UL 746A | |
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 120 ?m/m-?C | 66.7 ?in/in-?F | -40 - 23?C (-40 - 73?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C | 126 ?m/m-?C | 70 ?in/in-?F | 23 - 55?C (73 - 130?F); Parallel; ASTM E 831 | |
| CTE, linear 20?C | 130 ?m/m-?C | 72.2 ?in/in-?F | 23 - 55?C (73 - 130?F); Parallel; ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 120 ?m/m-?C | 66.7 ?in/in-?F | -40 - 23?C (-40 - 73?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 136 ?m/m-?C | 75.6 ?in/in-?F | 23 - 55?C (73 - 130?F); ASTM E 831 | |
| CTE, linear 20?C Transverse to Flow | 140 ?m/m-?C | 77.8 ?in/in-?F | 23 - 55?C (73 - 130?F); ISO 11359-1/-2 | |
| CTE, linear 20?C Transverse to Flow | 159 ?m/m-?C | 88.3 ?in/in-?F | 55 - 100?C (130 - 212?F); ISO 11359-1/-2 | |
| CTE, linear 100?C | 130 ?m/m-?C | 72.2 ?in/in-?F | 55 - 100?C (130 - 212?F); Parallel; ISO 11359-1/-2 | |
| Melting Point | 178 ?C | 352 ?F | ASTM D 3418 | |
| Melting Point | 178 ?C | 352 ?F | 10?C/min; ISO 11357-1/-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 ?C | 212 ?F | ISO 75-1/-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 ?C | 255 ?F | Not Annealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60 ?C | 140 ?F | ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61 ?C | 142 ?F | Not Annealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70 ?C | 158 ?F | Annealed; ISO 75-1/-2 | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 1.5mm; UL 746B | |
| UL RTI, Electrical | 105 ?C | 221 ?F | 3.0mm; UL 746B | |
| UL RTI, Mechanical with Impact | 85 ?C | 185 ?F | 1.5mm; UL 746B | |
| UL RTI, Mechanical with Impact | 85 ?C | 185 ?F | 3.0mm; UL 746B | |
| UL RTI, Mechanical without Impact | 85 ?C | 185 ?F | 3.0mm; UL 746B | |
| UL RTI, Mechanical without Impact | 85 ?C | 185 ?F | 1.5mm; UL 746B | |
| Flammability, UL94 | HB | HB | 3.0mm; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 3.0mm; UL94 | |
| Flammability, UL94 | HB | HB | 1.5mm; IEC 60695-11-10 | |
| Flammability, UL94 | HB | HB | 1.5mm; UL94 | |
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 | |
Processing Properties |
||||
|
||||
| Melt Temperature | 200 - 210 ?C | 392 - 410 ?F | ||
| Melt Temperature | 205 ?C | 401 ?F | Optimum | |
| Mold Temperature | 40 - 60 ?C | 104 - 140 ?F | ||
| Mold Temperature | 50 ?C | 122 ?F | Optimum | |
| Drying Temperature | 80 ?C | 176 ?F | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Dehumidified Dryer | |
| Moisture Content | Max 0.05 % | Max 0.05 % | ||
Descriptive Properties |
||||
|
||||
| Appearance | Natural Color | |||
| Drying | Recommended | If moisture content of resin exceeds recommended level | ||
| DuPont Product Category | Toughened Resins | |||
| DuPont Product Category | Unreinforced Resins | |||
| Extrudable | Coating | |||
| Extrudable | Tubing | |||
| Extrudable | Wire and Cable | |||
| Extrusion Blow Moldable | Yes | |||
| Features | Impact Modified | |||
| Features | Viscosity, High | |||
| Form | Pellets | |||
| Injection Moldable | Yes | |||
| Part Marking Code | >POM-HI< | ISO 11469 | ||
| Processing Method | Extrusion | |||
| Processing Method | Injection Molding | |||
| Region | Americas | |||
| Region | Asia/Pacific | |||
| Region | Europe | |||
| Resin Identification | POM-HI | ISO 1043 | ||
| Ultrasonic Weldable | Yes | |||
| Uses | Parts, Engineering | |||
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.