Solvay Advanced Polymers AMODEL?PPA A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded
Subcategory: Filled/Reinforced Thermoplastic; Polymer; Polyphthalamide; Thermoplastic
Close Analogs: This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
MatWeb has an entry for this material conditioned at 50% RH.
Material Notes:
Data provided by the manufacturer, Amoco Corporation.
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. AMODEL A-1115 HS resin can be easily processed using conventional equipment and methods.
No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
| Physical Properties | Metric | English | Comments | |
|
||||
| Density | 1.26 g/cc | 0.0455 lb/in? | ASTM D792 | |
| Water Absorption | 0.3 % | 0.3 % | 24 hrs. ASTM D570 | |
| Linear Mold Shrinkage | 0.006 cm/cm | 0.006 in/in | Flow Direction. ASTM D955 | |
Mechanical Properties |
||||
|
||||
| Hardness, Rockwell R | 127 | 127 | ASTM D785 | |
| Tensile Strength, Ultimate | 128 MPa | 18600 psi | ASTM D638 | |
| Elongation at Break | 2 % | 2 % | ASTM D638 | |
| Tensile Modulus | 8.3 GPa | 1200 ksi | ASTM D638 | |
| Flexural Modulus | 6.2 GPa | 899 ksi | ASTM D790 | |
| Flexural Yield Strength | 171 MPa | 24800 psi | ASTM D790 | |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 | |
| Poisson's Ratio | 0.41 | 0.41 | ||
| Shear Strength | 88 MPa | 12800 psi | ASTM D732 | |
| Izod Impact, Notched | 0.44 J/cm | 0.824 ft-lb/in | ASTM D256 | |
| Izod Impact, Unnotched | 4.38 J/cm | 8.21 ft-lb/in | ASTM D256 | |
Electrical Properties |
||||
|
||||
| Electrical Resistivity | 1e+016 ohm-cm | 1e+016 ohm-cm | ASTM D257 | |
| Dielectric Constant | 3.9 | 3.9 | at 1 MHz. ASTM D150 | |
| Dielectric Constant, Low Frequency | 4.2 | 4.2 | 60 Hz; ASTM D150 | |
| Dielectric Strength | 19 kV/mm | 483 kV/in | ASTM D149 | |
| Dissipation Factor | 0.02 | 0.02 | at 1 MHz. ASTM D150 | |
| Dissipation Factor, Low Frequency | 0.006 | 0.006 | 60 Hz; ASTM D150 | |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 | |
| Comparative Tracking Index | 550 V | 550 V | ||
Thermal Properties |
||||
|
||||
| CTE, linear 20?C | 35 ?m/m-?C | 19.4 ?in/in-?F | FD, 0-100?C (32-212?F); ASTM E831 | |
| CTE, linear 20?C Transverse to Flow | 59 ?m/m-?C | 32.8 ?in/in-?F | 0-100?C (32-212?F); ASTM E381 | |
| CTE, linear 250?C | 12 ?m/m-?C | 6.67 ?in/in-?F | FD, from 160-250?C (320-480?F); ASTM E831 | |
| CTE, linear 250?C | 95 ?m/m-?C | 52.8 ?in/in-?F | TD, from 160-250?C (320-480?F); ASTM E831 | |
| Melting Point | 310 ?C | 590 ?F | ASTM D3418 | |
| Maximum Service Temperature, Air | 160 ?C | 320 ?F | 20,000 hours continuous use; ASTM D3045 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 292 ?C | 558 ?F | ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 277 ?C | 531 ?F | ASTM D648 | |
| Flammability, UL94 | HB | HB | 3.2 mm | |
| Flammability, UL94 | HB | HB | 3.2 mm | |
Processing Properties |
||||
|
||||
| Processing Temperature | 321 - 343 ?C | 610 - 649 ?F | Melt Range; Injection Molding | |
|
||||
 Printer friendly version |
||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb